Abstract:The paper presents the results of tests of rapid solidification (RS) aluminum alloys with the addition of silicon (5%, 11%, and 20%). Casting by melt-spinning on the surface of an intensively cooled copper cylinder allowed to obtain a metallic material in the form of flakes, which were then consolidated in the process of pressing and direct extrusion. The effect of refinement on structural components after rapid solidification was determined. Rapidly solidified AlSi materials are characterized by a comparable size of Si particles, regardless of the silicon content, and the shape of these particles is close to spheroidal. Not only Si particles are fragmented, but also the Al-Si-Fe phase, which also changed its shape from irregular with sharp edges to regular and spherical. The melt-spinning process resulted in a fine-grained structure compared to materials obtained by gravity-casting and extrusion. The influence of the high-temperature compression test on the mechanical properties of rapidly solidified materials was analyzed, and the results were compared with those of gravity-cast materials. An increase in strength properties was found in the case of the AlSi5 RS alloy by 20%, in the case of AlSi11RS by 25%, and in the case of the alloy containing 20% Si by as much as 86% (tensile test). On the basis of the homogeneity of the particle distribution determined by the SEM method, it was found that rapid solidification is an effective method of increasing the strength properties and improving the plastic properties of Al-Si alloys.

Wear Characteristics of a Rapidly Solidified Al-Si Alloy under Dry Sliding

Dry sliding wear of MA/PM Al-10Ti alloy

Contributions of the Particulate Reinforcement to Dry Sliding Wear Resistance of Rapidly Solidified Al-Ti Alloys

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Effects of second phase on dry sliding wear of rapidly solidified Al-Ti alloy

Dry sliding wear of PM Al-10Ti alloy

Dry wear behavior of rheo-casting Al–16Si–4Cu–0.5Mg alloy

Wear-resistance mechanism of an Al–12Si alloy reinforced with aluminosilicate short fibers

Effect of Cold Deformation on Low Speed Sliding Wear of Al-10Ti Alloy

Wear behavior of Mg–10Y–4Gd–1.5Zn–0.4Zr alloy

Effects of silicon content and test conditions on the dry wear behaviour of Zn–30Al–3Cu–(0–5)Si Alloys

A Comparison of the Sliding Wear Behavior of a Hypereutectic Al–Si Alloy Prepared by Spray-Deposition and Conventional Casting Methods

Microstructure and Mechanical Properties of Al-Si Alloys Produced by Rapid Solidification and Hot Extrusion

Dry Sliding Wear Behaviour of Al–7.6Si–xZr Alloys: Understanding the Impact of Zr on Wear Characteristics, Mechanics, and Transition

Evaluation of dry sliding wear behavior of silicon particles reinforced aluminum matrix composites

Microstructure and Sliding Wear Behavior of PM Alloy Al10Ti after Thermal Exposure

Study on Microstructure, Mechanical Properties and Erosion Characteristics of Al-Si Alloy Manufactured by Continuous Casting Direct Rolling Process

Dry Sliding Wear Properties of Rheo-diecasting Hypereutectic Al-Si Alloy with High Iron Content

Effects of Si Alloying and T6 Treatment on Mechanical Properties and Wear Resistance of ZA27 Alloys

Dry sliding wear behavior of cast Mg–11Y–5Gd–2Zn magnesium alloy

Wear Behavior of a Heat-Treatable Al-3.5Cu-1.5Mg-1Si Alloy Manufactured by Selective Laser Melting