Dry Sliding Wear Behaviour of Al–7.6Si–xZr Alloys: Understanding the Impact of Zr on Wear Characteristics, Mechanics, and Transition

Prosanta Biswas,Manas Kumar Mondal

DOI: https://doi.org/10.1007/s40962-024-01296-7

2024-03-14

International Journal of Metalcasting

Abstract:This study investigates the dry sliding wear behaviour of Al–7.6Si– x Zr ( x = 0.0, 0.1, 0.2, and 0.3) alloys under different applied loads of 19.6 N, 39.2 N, and 58.8 N, aiming to understand the underlying wear mechanism of the alloys. The inclusion of Zr in the Al–7.6Si alloy led to the formation of in situ ZrSi and ZrSi 2 compounds, serving as nucleation sites that result in finer and granular α-Al and acicular and fibrous eutectic Si formation. This Zr modification also contributed to improving the alloy's bulk hardness. Wear test results indicated that the proportion of Zr and wear test loads was important factors influencing the cumulative wear loss (CWL) and coefficient of friction (COF). The wear resistance of the Al–7.6Si– x Zr alloys decreased with an increase in the wear test load but increased with an increase in the sliding distance. The primary wear mechanisms were abrasive, adhesive, and oxidative wear, and they exhibited significant variations depending on the concentration of Zr in the alloy. The addition of Zr significantly improved the wear resistance of the Al–7.6Si alloy, and the wear resistance increased as the Zr concentration increased. The wear maps depicted the transitional stages between different wear mechanisms under varying loads and sliding distances. Graphical

metallurgy & metallurgical engineering