Abstract:Hypereutectic Al-Si alloys are used as material for the engine block and cylinder liners in automobiles. Wear behaviour of hypereutectic Al-Si alloy system changes significantly with applied normal load in both mild wear and severe wear regime. Significant improvement in wear resistance can be obtained by exposing silicon particles through the chemical etching process. For Al-25% Si alloys, most studies are reported in mild and ultra-mild wear regime. In the present work, the wear of exposed silicon particles with varying load and speed in severe wear regime was investigated under the unidirectional sliding condition and bi-directional sliding condition using a pin-on-disk tribometer (POD) and a linear reciprocating tribometer (LRT), respectively. Rapidly solidified and T6 heat-treated Al-25Si alloy was polished and etched using 5% NaOH solution to expose the silicon particles. Experiments were carried out with normal loads varying from 40 N to 120 N in dry sliding conditions. Sliding speeds of 0.8 m/s and 1.5 m/s were applied for each load in case of a pin on disk tribometer whereas, in an LRT, the sliding velocities were 0.2 m/s and 0.45 m/s respectively for each set of the load. The surface topography was measured by means of a 3-D optical profilometer, and surface morphology was analyzed using SEM images. It was observed that at higher loads, larger Si particles were fractured and pushed into the matrix. Fractured silicon particles, along with smaller particles, were embedded into the matrix, thereby increasing the silicon concentration in the wear region. The comparison of the experimental results of unidirectional and bi-directional sliding that reveal the change in surface morphology of silicon particles, the friction characteristics at the interface, variation of surface 3-D roughness parameters, the wear rate and wear mechanisms of Al-25% Si alloys are analyzed and reported in the study.

Wear Properties Analysis on Al-Based Automotive Alloy with Varied Levels of Si in Dry, 3.5% NaCl and Seawater Corrosive Environments

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Effects of silicon content and test conditions on the dry wear behaviour of Zn–30Al–3Cu–(0–5)Si Alloys

Corrosive Wear of Alumina Particles Reinforced Al–Si Alloy Composites

Electrochemical corrosion performance of Si-doped Al-based automotive alloy in 0.1 M NaCl solution

Effects of Some Material and Experimental Variables on the Slurry Wear Characteristics of Zinc-Aluminum Alloys

Investigating the load and temperature-dependent dry sliding wear performance of Al–12Ce alloys with Si and Mg additions

Effect of Si on Phase Equilibria, Mechanical Properties and Tribological Behaviour of Al-Cu Alloy

Effect of Si Content on the Dry Sliding Wear Properties of Spray-Deposited Al–Si Alloy

Temperature effect on the friction and wear of an Al-60Si alloy

Tribological behaviour of hypereutectic Al-Si automotive cylinder liner material under dry sliding wear condition in severe wear regime

Wear and Corrosion Properties of 316L-SiC Composite Coating Deposited by Cold Spray on Magnesium Alloy

Wear Behavior of a Heat-Treatable Al-3.5Cu-1.5Mg-1Si Alloy Manufactured by Selective Laser Melting

Dry Sliding Wear Behaviour of Al–7.6Si–xZr Alloys: Understanding the Impact of Zr on Wear Characteristics, Mechanics, and Transition

Effect of Si3N4 Ceramic Particulates on Mechanical, Thermal, Thermo-Mechanical and Sliding Wear Performance of AA2024 Alloy Composites

The Effect of Wear Environment Temperature on the Wear Behavior and Friction Coefficient of SiCw/Al Composite

Wear Behavior of the Friction Stir Alloyed AZ31 Mg at Different Volume Fractions of Al Particles Reinforcement and Its Enhanced Quality Attributes

Metallographic Study and Sliding Wear Optimization of Nano Si3N4 Reinforced High-Strength Al Metal Matrix Composites

A comparative analysis of different surface tribological and electrochemical properties of TiAlN, TiAlSiN, and CrAlN thin film coatings in seawater

Effect of SiC Weight Percentage on Tribological Characteristics of Al7075/SiC Composites

Influence of eutectic-Si in as-cast and fibrous-eutectic-Si in LPBF-processed AlSi10Mg alloys on wear and corrosion behaviors treated with direct aging route