Activated Sintering Process of a Tungsten Heavy Alloy

Fan Jinglian,Qu Xuanhui,Huang Baiyun,Li I. Yimin
1999-01-01
Rare Metal Materials and Engineering
Abstract:In order to decrease sintering temperature and enhance the properties of a tungsten heavy alloy W-Ni-Fe by means of activated sintering, such as activated liquid phase sintering and mechanical activation,the following tests have been made: (1)Adding Co and Mn powders into the alloy to reduce the matrix melting temperature and accelerate the dissolution and diffusion of W into the matrix-binder phase (i.e. activated liquid phase sintering); (2) High energy ball milling of the initial powder mixtures (i.e. mechanical alloying (MA)). The results show that the liquid phase sintering of 95W-3.5Ni-1.5Fe is activated by the Co addition. After adding Co,not only the sintering temperature decreased by 30%similar to 50 degrees C,but also the mechanical properties are improved and stabilized. Although the Mn addition has very low melting temperature, the same alloy is not activated by the Mn addition due to solubility limitation. During MA, there are several activated mechanisms, including fine grain activation mechanical activation and prealloying activation. After MA the sintering temperature of the nanocrystalline composite decreases to below melting temperature (1465 degrees C) of the matrix,and the alloy has high tensile properties.
What problem does this paper attempt to address?