New low-temperature sintering tungsten-nickel-antimony alloy: Microstructure evolution and mechanical properties
Amir Pahlevani,Hamidreza Mohammadian Semnani,Hassan Abdoos
DOI: https://doi.org/10.1016/j.ijrmhm.2022.105952
IF: 4.804
2022-11-01
International Journal of Refractory Metals and Hard Materials
Abstract:This study determined the possibility of reducing sintering temperature by designing a new tungsten heavy alloy (WHA). For this purpose, 90 W-(10-X)Ni-XSb alloys with different Sb (X = 2.4, 3.2, and 4) were sintered at 1100, 1200, 1300, and 1400 °C for 60 min. SEM equipped with energy-dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD)analysis was used to evaluate the microstructure and composition of sintered alloys. The samples were then examined for their density, hardness, and mechanical properties. The relative densities of the 90 W-6.8Ni-3.2Sb alloy sintered at 1200 °C and the 90 W-7.6Ni-2.4Sb alloy sintered at 1300 °C were achieved over 99%. The maximum relative density (99.51%) was achieved in 90 W–6.8Ni–3.2Sb alloys sintered at 1300 °C. The tungsten particle size in this alloy was about 27.8 μm. With increasing of antimony, the tungsten particle size and relative density initially increased and then decreased again, while the opposite was observed for contiguity. The x-ray diffraction pattern revealed that the Ni3Sb phase developed in the matrix phase as the antimony content increased. In addition, when Sb rose, the compressive yield strength fell and the hardness increased. The compressive yield strength of alloys containing 2.4, 3.2, and 4 wt% Sb was 1325, 1322, and 1251 MPa, respectively. The density, hardness, and compressive yield strength of the W-Ni-Sb alloys were comparable to that of the conventional W-Ni-Fe alloys, while the sintering temperature was lower.
materials science, multidisciplinary,metallurgy & metallurgical engineering