Effect of stress on the nucleation and evolution of Mo-rich Laves phase in 9.5Cr-1.5MoCoVNbNB heat-resistant steel during tensile rupture at 620 °C
Huifang Yin,Wenqing Ge,Fengshi Yin,Jiqing Zhao,Gang Yang,Hansheng Bao,Li Zhou
DOI: https://doi.org/10.1016/j.matchar.2022.112565
IF: 4.537
2022-12-10
Materials Characterization
Abstract:In this study, the nucleation and evolution of Mo-rich Laves phase particles in 9.5Cr-1.5MoCoVNbNB heat-resistant steel during tensile rupture testing at 620 °C were investigated using transmission electron microscopy (TEM) and atom probe tomography (APT). Laves phase particles have two nucleation mechanisms along the martensite lath boundary:(1) the formation of Laves phase particles alone on the boundary and their growth in one orientation and (2) the nucleation of Laves phase particles adjacent to M 23 C 6 carbides without a specific growth orientation. Analysis of the TEM, energy dispersive X-ray spectroscopy, (EDS), and APT results revealed that deformation facilitated pipe diffusion and provided more sites for the nucleation of the Mo-rich Laves phase. In addition, it was found that stress resulted in a different evolution of the Laves phase adjacent to the M 23 C 6 carbides compared to that occurring during aging at the same temperature. Further, the Laves phase particles nucleated at the interface of the coarsening M 23 C 6 carbides and eventually wrapped around the nearby carbides, resulting in the elemental redistribution of Mo and Cr. In particular, the APT results indicate that the nucleation of the Mo-rich Laves phase on the M 23 C 6 carbide interface during tensile rupture is because of Si and P enrichment around the carbides.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing