Abstract:High-chromium martensitic steels are a promising material for the production of elements of boilers and steam pipelines, as well as blades and rotors of steam turbines for new coal-burning thermal generating units. The use of such materials will give an opportunity for the transition to ultra-supercritical steam parameters (temperature of 600–620 °C and pressure of 25–30 MPa), which will allow increasing the efficiency of generating units to 45 %. Modifications of the chemical composition of high-chromium steels have led to significant improvements of high-temperature properties such as 100,000 h creep strength and 1 % creep limit, while resistance to softening due to low-cycle fatigue remains understudied in this field. This work covers the study of low-cycle fatigue at room temperature with different amplitudes of deformation of martensitic high-chromium 10%Cr–3%Co–2%W–0.5%Mo–0.2%Cu–0.2%Re–0.003%N–0.01%B steel. The steel was pre-subjected to normalizing at 1050 °С followed by tempering at 770 °С. After heat treatment, the steel structure was a tempered martensitic lath structure stabilised by the particles of secondary phases of M23C6 carbides, NbX carbonitrides, and M6C carbides. The average width of martensite laths was 380 nm, and the dislocation density was 1.4×1014 m−2. At low-cycle fatigue, with an increase in the strain amplitude from 0.2 to 1 %, the number of cycles before failure significantly decreases, and the value of plastic deformation in the middle of the number of loading cycles significantly increases. Maximum softening (18 %) is observed at a strain amplitude of 1 % in the middle of the number of loading cycles. In general, the steel structure after low-cycle fatigue tests does not undergo significant changes: the width of the laths increases by 18 % at a strain amplitude of more than 0.3 %, while the dislocation density remains at a rather high level (about 1014 m−2) at all strain amplitudes.

On the Fracture Behavior of a Creep Resistant 10% Cr Steel with High Boron and Low Nitrogen Contents at Low Temperatures

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Revealing influence of warm bending on creep performance of heat-resistant 2.25Cr-1Mo-0.25 V steel

Temperature-Dependent Deformation and Fracture Properties of Low-Carbon Martensitic Steel in Different Stress States

Deterioration of Mechanical Properties of Novel Constructional Steel Material at Elevated Temperatures

Low-cycle fatigue of 10 % Cr steel with high boron content at room temperature

Microstructural Evolution of a Re-Containing 10% Cr-3Co-3W Steel during Creep at Elevated Temperature

Temperature dependence of the deformation behavior and mechanical properties of a Fe–Mn–Al–C low-density steel for cryogenic application

Experimental study on fracture resistant design method for steel structural components at low temperature

Advances in the mechanism of cleavage fracture of low alloy steel at low temperature. Part I: Critical event

High temperature creep behavior of a novel Cr18Ni9NbTiN austenitic stainless steel

Tension Deformation Mechanism and Fracture Characteristics of High Nitrogen Steel 6cr21mn10movnbn at 25–800°C

ON THE TIME-DEPENDENT MATERIAL FRACTURE TOUGHNESS AT HIGH TEMPERATURE

Crack propagation behavior of dual-phase steel at low temperature

Flow Behaviour and Ductile Fracture Toughness of a High Toughness Steel

Creep Resistance and Structure of 10% Cr–3% Сo–2% W–0.29% Cu–0.17% Re Steel with Low Nitrogen and High Boron Contents for Unit Components of Coal Power Plants

Cryogenic Toughness in a Low-Cost Austenitic Steel

Experimental Study on Fracture Toughness of Q460C the High-Strength Construction Steel at Low Temperature

Investigation of Residual Stress Effect on Cleavage Fracture Toughness in the Transition Temperature Region by Considering the Crack-Tip Constraint

Effects of Long-Term Creep at Elevated Temperatures on Rupture Ductility in 9Cr-1Mo-v-nb-n Steel

Quasi-in-situ observations of crack propagation and microstructure evolution of high manganese austenitic steel at −196 °C