Crack propagation behavior of dual-phase steel at low temperature
Chaoping Jiang,Hongchuan Ma,Yongnan Chen,Nan Wang,Qinyang Zhao,Gang Wu,Lixia Zhu,Jinheng Luo,Yongqing Zhao
DOI: https://doi.org/10.1016/j.ijfatigue.2021.106633
IF: 5.489
2022-02-01
International Journal of Fatigue
Abstract:In this work, the crack propagation behavior and mechanism of dual-phase steel were studied under low temperature environment. The results show that the strength of dual-phase steel increases from −20 °C to −60 °C, and the fracture toughness presents the opposite trend. When the crack began to extend at low temperature, the size of plastic zone at the crack-tip is reduced, inducing the opening displacement rate, strain rate and temperature-strain parameters are reduced, which shows the extreme sensitivity to ambient temperature. More importantly, the fracture of dual-phase steel presents the transgranular fracture along {101} and {111} crystal planes, due to the accumulation of dislocation density. Therefore, the crack propagation of dual-phase steel at low temperature is caused by the dislocation accumulation and movement behaviors.
materials science, multidisciplinary,engineering, mechanical