Abstract:Dissimilar metal welds (DMWs) between high-Cr martensitic heat-resistant steels and nickel-based alloys with nickel-based filler metals are widely used in fossil-fired power plants. Reports of premature failures of DMW joints have attracted considerable attention as such occurrences in the field can lead to significant economic loss and safety issues. Moreover, a comprehensive understanding of the high-temperature performance of new types of DMWs is lacking. In this work, creep tests were conducted over a stress range of 140-260 MPa at of 600 and 620 'C. A shift in the fracture location with variations in stress was observed, with three typical failure modes. At high stress levels (240-260 MPa), the DMW fractured in the base metal (BM) of martensitic steel, accompanied by a large degree of plastic deformation. At intermediate stress levels (200-240 MPa), the DMW fractured in the fine-grained heat-affected zone (FGHAZ) and the inter-critical heat-affected zone (ICHAZ), with creep cavities around coarsened carbides, indicating a typical type IV crack. At low stress levels (140-200 MPa), the DMW fractured in a mixed mode involving three stages. First, a crack initiated at the interface between the nickel-based weld metal and the martensitic steel, which was attributed to the interaction between the oxidation behavior of the martensitic steels and the thermal stress arising from the mismatch in the coefficients of thermal expansion. Second, the crack deflected into the FGHAZ/ICHAZ and developed into a type IV crack mode. Finally, the crack propagated into the adjacent BM, featuring significant plastic deformation. In addition, in the stress-LMP (Larson-Miller parameter) plot, the creep life at a relatively low stress level was shorter than that predicted by linear extrapolation of the data obtained at a high stress level, indicating a premature failure tendency at low stress. This premature failure tendency can be attributed to microstructure degradation in HAZs and preferential oxidation at the interface at low stress levels.

Two Fatigue Fracture Modes at Different Temperatures of 10%cr Heat-Resistant Steel Weldment Filled with Ni-Based Alloy

Fatigue Crack Growth Mechanism of Ni-based Weld Metal in a 9% Ni Steel Joint

The Influence of Microstructure Evolution in Thick Plate 9%ni Steel Submerged Arc Welding Joint on Fracture Toughness Properties

Low-cycle Fatigue Behaviors of a New Type of 10% Cr Martensitic Steel and Welded Joint with Ni-based Weld Metal

Low-cycle Fatigue and Fracture Behaviour of 9%ni Steel Flux Cored Arc Welding Joint at Cryogenic Temperature

Near-threshold fatigue crack growth behavior of 10% Cr martensitic steel welded joint with 9% Cr weld metal in high temperature air

Microstructural Characteristics and Low Cycle Fatigue Properties at 230 °C of Different Weld Zone Materials from a 100 Mm Thick Dissimilar Weld of Ultra-Supercritical Rotor Steel

Microstructure Characterization and HCF Fracture Mode Transition for Modified 9Cr-1Mo Dissimilarly Welded Joint at Different Elevated Temperatures

Mixed Mode Fatigue Crack Growth Behavior of Ni-Cr-Mo-V High Strength Steel Weldments

Failure Mechanisms and Design of Dissimilar Welds of 9%cr and CrMoV Steels Up to Very High Cycle Fatigue Regime

Effect of Temperature on High‐cycle Fatigue and Very High Cycle Fatigue Behaviours of a Low‐strength Cr–Ni–Mo–V Steel Welded Joint

Effect of long-term aging on near-threshold fatigue crack growth of Ni–Cr–Mo–V steel welds

Understanding of Fatigue Crack Growth Behavior in Welded Joint of a New Generation Ni-Cr-Mo-V High Strength Steel

Near-threshold Fatigue Crack Growth Behavior of the Weld Metal and Heat-Affected Zone in an Ex-Service CrMoV Steel Joint

Fatigue crack growth behavior of Ni-Cr-Mo-V steel welded joints considering strength mismatch effect

Very High Cycle Fatigue Behavior of 25cr2ni2mov Steel Welded Joint

High-Temperature Fatigue Behavior of Inertia Friction Welded Joints of GH4065A Ni-Based Superalloy

High temperature damage development in Ni-alloy/steel dissimilar metal welds

Fracture Location Shift of Dissimilar Metal Welds under Coupled Thermal-Stress Effect

Microstructure and Mechanical Characteristics of Dissimilar TIG Welded 9% Cr Heat-Resistant Steels Joints

Microstructure and Property of Ni76Cr19AlTi Side in Inertia Friction Weld Joint of the Superalloy Ni76Cr19AlTi and the Martensite Stainless Steel 4Cr10si2mo