Fatigue Crack Growth Mechanism of Ni-based Weld Metal in a 9% Ni Steel Joint

Kejian Li,Xue Wang,Shao-Shi Rui,Xiaogang Li,Shanlin Li,Qixing Sun,Yu Zhang,Zhipeng Cai

DOI: https://doi.org/10.1016/j.msea.2021.142485

2022-01-01

Abstract:This research focused on the impact of temperature and driving force Delta K on the fatigue crack growth (FCG) mechanism of C-276 Ni-based weld metal in a 9% Ni steel joint. On one hand, the FCG resistance increased due to higher yield strength at 77 K than at room temperature (RT), and the decrease of FCG rate can be well explained by Weertman's model. On the other hand, critical Delta K values (37.5 MPa m(1/2) at 77 K and 30.2 MPa m(1/2) at RT) existed in the process of FCG, accompanied by the transition of FCG mechanism at both 77 K and Delta T. In detail, the fatigue crack mainly propagated in a quasi-cleavage mode at a lower Delta K level at 77 K, in a single-slip mode at a higher Delta K level at 77 K or a lower Delta K level at Delta T, and in a multi-slip mode at a higher AK level at Delta T. Furthermore, the dislocation-precipitate interaction was enhanced and even provided favourable locations for FCG at a higher Delta K level at RT, leading crack to propagate via linking after the formation of micro-cracks and micro-voids near precipitates.