Abstract:A high-temperature, high-cycle fatigue test was conducted on a nickel-based single-crystal superalloy with a pore structure. Optical and scanning electron microscopy were utilized to examine the crack propagation paths and fatigue fracture surfaces at the macro and micro scales. The analysis of crack initiation and propagation related to the pore structure facilitated the development of a crack shape factor reflecting these distinct fracture behaviors. Predictions about the high-cycle fatigue stress experienced by the specimen were made, accompanied by an error analysis, providing critical insights for precise stress calculations and structural optimization in engine blade design. The results reveal that high-cycle fatigue cracks originate from corner cracks at pore edges, with the initial propagation displaying smooth crystallographic plane features. Subsequent stages show clear fatigue arc patterns in the propagation zones. The fracture surface exhibits the significant layering of oxide layers, primarily composed of NiO, with traces of CoO displaying columnar growth. AL2O3 is predominantly found at the interfaces between the matrix and oxide layers. Short and straight dislocations near the oxide layers and within the matrix suggest that dislocation multiplication and planar slip dominate the slip mechanisms in this alloy. The orientation of the fracture surface is mainly perpendicular to the load direction, with minor inclined facets in localized areas. Correlations were established between the plastic zone dimensions at the crack tips and the corresponding fatigue stresses. Without grain boundaries in single-crystal alloys, these dimensions are easily derived as parameters for fatigue stress analysis. The selected crack shape factor, "elliptical corner crack at pore edges", captures the initiation and propagation traits relevant to porous structures. Subsequent calculations, accounting for the impact of oxide layers on stress assessments, indicated an error ratio ranging from 1.00 to 1.21 compared to nominal stress values.

Fatigue crack nucleation behavior in nickel-based PM alloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Study on Microstructure and Fatigue Properties of FGH96 Nickel-Based Superalloy

Study of Fatigue Crack Initiation and the Propagation Mechanism Induced by Pores in a Powder Metallurgy Nickel-Based FGH96 Superalloy

Thermo-mechanical fatigue crack growth in a nickel-based powder metallurgy superalloy

Elevating Fatigue Life in Nickel-Based Superalloys Through Suppression of Persistent Slip Bands/markings Via High-Density Pulsed Electric Current Treatment

Micro-strain and cyclic slip accumulation in a polycrystalline nickel-based superalloy

Quantitative Study of High-Frequency Fatigue Hole-Edge Stresses in Nickel-Based Single-Crystal Superalloy

Effect of Stress Ratio on the Fatigue Crack Propagation Behavior of the Nickel-based GH4169 Alloy

In-situ SEM study on fatigue crack behavior of a nickel-based single crystal alloy at 950 °C and 1050 °C

Fatigue Life Assessment of a Porous Casting Nickel-Based Superalloy Based on Fracture Mechanics Methodology

Evolution of fatigue mechanical properties and micro defects in nickel-based single crystal superalloys: A molecular dynamics research

Microstructural insights into fatigue short crack propagation resistance and rate fluctuation in a Ni-based superalloy manufactured by Laser powder bed fusion

Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 C by In Situ SEM Studies

Multi-stage dwell fatigue crack growth behaviors in a nickel-based superalloy at elevated temperature

Fractograph examination of superalloy GH4169 at low cycle fatigue

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Fatigue crack nucleation and microstructurally small crack growth mechanisms in high strength aluminum alloys

Ex-situ observation of the short crack initiation and propagation behaviour of nickel-base wrought alloy Inconel 718 for critical rotating components under fatigue conditions at elevated temperatures

Fretting fatigue damage mechanism of Nickel-based single crystal superalloys at high temperature