Abstract:In this study, the dynamic recrystallization behavior of low‐alloy steel used in reactor pressure vessels is examined. Elevated temperatures and phase coarsening degrade its strength–toughness relationship. Using computational thermodynamics and the CALculation of PHAse Diagram framework, phase stability and mechanical properties are predicted, enabling the optimization of alloy composition and processing for improved high‐temperature, high‐pressure performance. The dynamic recrystallization (DRX) behavior of SA508‐III steel, a critical material for reactor pressure vessels (RPVs) normally treated by hot forging, is thoroughly examined in this article. In the investigation, elevated temperatures and the coarsening of metallic phases and carbides are revealed to contribute to the degradation of the steel's strength–toughness relationship. Utilizing computational thermodynamics, the stability of secondary phases, including carbides and brittle inclusions, is simulated to enable precise phase equilibrium calculations and accurate prediction of key mechanical properties such as yield strength, tensile strength, and hardness. These simulations facilitated targeted modifications to the alloy composition to enhance the steel's strength and hardenability under high‐temperature, high‐pressure conditions. In this study, alloy composition and processing parameters within the CALculation of PHAse Diagram framework, utilizing the ThermoCalc and JMatPro software packages, are optimized. In the microstructural investigations conducted under various isothermal deformation conditions (1173–1473 K) and strain rates (0.001–1 s−1), it is demonstrated that DRX mechanisms led to varied grain size developments, with a critical strain rate identified at 0.01 s−1 during high‐temperature deformations. In these findings, significant insights are provided into optimizing the mechanical performance of SA508‐III steel for RPV applications.

Assessment of tensile deformation and fracture toughness behavior of 10Cr steel at ambient and high temperatures

Experimental Investigations On Mechanical Properties Of A High Cr Ferritic Steel For Usc Steam Turbine Rotor

Deformation Characteristics of A High Chromium, Power Plant Steel at Elevated Temperatures

Deterioration of Mechanical Properties of Novel Constructional Steel Material at Elevated Temperatures

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Evaluation of the time dependent failure assessment curves for 10CrMo910 and 316 SS at 550°C

Low Cycle Fatigue of 9-12% Cr Steel at Elevated Temperature: Cyclic Deformation Behavior and Life Assessment

ON THE TIME-DEPENDENT MATERIAL FRACTURE TOUGHNESS AT HIGH TEMPERATURE

Deformation and Damage Behavior of a 1Cr-Cast Steel Under Multiaxial Loading at Elevated Temperatures

Constitutive Modeling for Elevated Temperature Flow Behavior of 30cr2ni4mov Ultra-super-crical Rotor Steel

Material Degradation And Creep Damage Of Aging Components At High Temperature

Prediction of multiaxial creep ductility for a USC steam turbine rotor steel at 600 degrees C

Hot Deformation Behavior and Thermal Processing Map of 630°C Ultra-Supercritical Rotor Steel

An experimental study into the degradation of elastic, plastic and fracture properties of a pre-corroded ductile material at elevated temperatures

Recrystallization Behavior of Computationally Optimized Low‐Alloy Steel at Various Temperatures and Strain Rates

Ductile Fracture in ASTM A992 Steel Tensile Specimens at Elevated Temperatures

Analysis on Premature Fracture of X12CrMoWVNbN10-1-1 Steel for USC Steam Turbine Rotors

RECENT PROGRESS IN HIGH TEMPERATURE MECHANICAL BEHAVIOR OF MATERIALS AND STRUCTURES

Calibration of the Johnson–Cook model at high temperatures for an Ultra-High Strength CrNiMoV Steel

Fracture behavior of high-strength steels at elevated temperatures

Creep Behavior and Cavitation Evolution of 15crmog Steel at High Temperatures