Microstructure evolution of weld root in dissimilar weld metal in S690QL high-strength steel under multiple welding thermal cycles
Bin Zhang,Weidong Mu,Hailong Liu,Geng Xie,Yan Cai
DOI: https://doi.org/10.1007/s10853-023-08478-4
IF: 4.5
2023-06-28
Journal of Materials Science
Abstract:For the welded joints of S690QL high-strength steel, determining the local brittle zone (LBZ) in dissimilar weld metal, understanding the microstructure evolution caused by multiple welding thermal cycles and element diffusion is significant to evaluate the safe service. However, microstructure evolution in weld root is ignored in previous studies. Here in this article, we utilized various characterization methods to elucidate the effect of multiple thermal cycle on weld root microevolution. The results of the impact test and the crack tip opening displacement (CTOD) test show that there is an LBZ in the root weld pass. The effects of welding multiple thermal cycle and base metal element dilution on the microstructure evolution of root zone were analyzed. The results indicate that although the microhardness of root zone is intermediate between SAW zone and SMAW zone, the impact energy of root zone is ~ 92 J compared with SAW zone (~ 133 J) and SMAW zone (~ 121 J), which is the LBZ. Due to the dilution of the base metal, C, Cr, and Ni elements diffuse into the root pass. Meanwhile, under multiple thermal cycles, the grain coarsens, the proportion of high-angle grain boundaries decreases, and martensite-austenite (M-A) constituents grow and evolve into large-size blocks, which has two types substructure, contributing to the impact toughness reduction of root zone. Furthermore, M-A constituents show different fracture behaviors under fast loading and slow loading. This study not only reveals the evolution behavior of M-A constituents, but also provides a design reference for the microstructure optimization and property improvement of 690 MPa grade high-strength steel welded joints.
materials science, multidisciplinary