Abstract:Silica aerogel has been formed using CO2 gas as the gelation agent through the low-cost ambient pressure drying technique. With water wash and the following solvent exchange process for Na+ removal, this synthesis route has no ion exchange resin used and becomes more straightforward. In order to reduce the silica particle and pore sizes, different hydrolysis-condensation rate control agents including dimethylformamide (DMF), methyl-triethoxysilane (TMES), Glycerol and methyltrimethoxylsilane (MTMS) have been applied to modify the structural groups of silica network. Results show that MTMS is the most effective control agent and the optimized MTMS/silica sol volume ratio has been found at 1% by testing the specific surface area of the aerogel. In addition, the effects of chlorotrimethylsilane (TMCS) amount and the calcining temperature on the physicochemical properties of the aerogel have been also investigated. When the TMCS/silica sol volume ratio is 0.4, Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) measurement shows that there is an apprent exothermic peak at calcining temperture of 420 degrees C, caused by the transformation of Si-CH3 group to Si-OH group. X-ray photoelectric spectroscopy (XPS) results show that the percentages of Si-C(-H) bonds with binding energy of 102.4 eV have decreased from 25.5% to 7.2% after 420 degrees C calcining. The contact angle of the as-dried aerogel is as high as 154 and dramatically decreases to ca. 109 degrees after calcining at 450 degrees C. The pore volume and BET specific surface area both increase first and then decrease with the increase of calcining temperature, and the pore volume reaches the maxmium of 1.45 cm(3)/g at 400 degrees C and it confirms Si-CH3 group release. This study offers a new facile route to the synthesis of silica aerogel and presents a promising way of the cost-effective large-scale manufacturing.

Structure modification of silica aerogel

Springback effect and structural features during the drying of silica aerogels tracked by in-situ synchrotron X-ray scattering

Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying

Preparation of Alumina Aerogel via Supercritical Method

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Improvement of the Thermal Insulation Performance of Silica Aerogel by Proper Heat Treatment: Microporous Structures Changes and Pyrolysis Mechanism

Effects of Surfactants on the Synthesis of Silica Aerogels Prepared by Ambient Pressure Drying

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

The Effects of Microstructure on Optical and Thermal Properties of Porous Silica Films

Preparation of High-Temperature Resistant Aerogels by Incorporating Aluminum Sol into Composite Silica Sources Using Ambient Pressure Drying

Synthesis and characterization of silica aerogels by a novel fast ambient pressure drying process

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

Synthesis of high specific surface area silica aerogel from rice husk ash via ambient pressure drying

Preparation of Silica Aerogels Monoliths from Hydrophobic Silica Gels and Pluronic10R5 via Sol–Gel Process

Preparation and Properties of Highly Transparent SiO2 Aerogels for Thermal Insulation

Influence of thermal annealing on structural properties of silica aerogel super insulation material

Synthesis of Alumina Aerogels by Ambient Drying Method and Control of Their Structures

Silica aerogel; synthesis, properties and characterization

Postsynthetic modification of yttria‐stabilized zirconia aerogels with silica coatings for enhanced thermal stability

A study of morphological properties of SiO2 aerogels obtained at different temperatures

Study on Silica Aerogel Modified by Trimethylchlorosilane