Abstract:The stress state is a crucial parameter for the design of innovative microelectromechanical systems based on silicon carbide (SiC) material. Hence, mechanical properties of such structures highly depend on the fabrication process. Despite significant progresses in thin-film growth and fabrication process, monitoring the strain of the suspended SiC thin-films is still challenging. However, 3C-SiC membranes on silicon (Si) substrates have been demonstrated, but due to the low quality of the SiC/Si heteroepitaxy, high levels of residual strains were always observed. In order to achieve promising self-standing films with low residual stress, an alternative micromachining technique based on electrochemical etching of high quality homoepitaxy 4H-SiC layers was evaluated. This work is dedicated to the determination of their mechanical properties and more specifically, to the characterization of a 4H-SiC freestanding film with a circular shape. An inverse problem method was implemented, where experimental results obtained from bulge test are fitted with theoretical static load-deflection curves of the stressed membrane. To assess data validity, the dynamic behavior of the membrane was also investigated: Experimentally, by means of laser Doppler vibrometry (LDV) and theoretically, by means of finite element computations. The two methods provided very similar results since one obtained a Young's modulus of 410 GPa and a residual stress value of 41 MPa from bulge test against 400 GPa and 30 MPa for the LDV analysis. The determined Young's modulus is in good agreement with literature values. Moreover, residual stress values demonstrate that the fabrication of low-stressed SiC films is achievable thanks to the micromachining process developed.

Measurement of Young's modulus and residual stress of silicon microstructures

Measurement Of Young'S Modulus And Residual Stress Of Micromembranes

A Method of Measuring Young's Modulus and Residual Stress in Typical MEMS Structures Using a Surface Profilometer

Characterization of the Young's Modulus and Residual Stresses for a Sputtered Silicon Oxynitride Film Using Micro-Structures

Measurement of Young's modulus and residual stress of copper film electroplated on silicon wafer

Study of techniques for measuring residual stress in micromachined films

The resolution and repeatability of stress measurement by Raman and EBSD in silicon

A simple analytical method for residual stress measurement on suspended MEM structures using surface profilometry

Young's Modulus Characterization of Nano-Level Silicon Nanomembrane

Mechanical Properties of Mono-crystalline Silicon Thin Films Measured by Different Methods

Measurements of Residual Stresses in Al Film/silicon Nitride Substrate Microcantilever Beam Systems

Micro-Raman spectroscopy measurement of stress in silicon

Residual stress measurement method in MEMS microbeams using frequency shift data

New Methods for Measuring Mechanical Properties of Thin Films in Micromachining: Beam Pull-in Voltage (VPI) Method and Long Beam Deflection (LBD) Method

Investigation of the Young's Modulus and the Residual Stress of 4H-SiC Circular Membranes on 4H-SiC Substrates

Experimental and Theoretical Study of Young Modulus in Micromachined Polysilicon Films

Characterization of Residual Stress in SOI Wafers by Using MEMS Cantilever Beams

Measurements of Residual Stresses in the Parylene C Film/Silicon Substrate Using A Microcantilever Beam

Measurement of young's modulus and residual stress of nanobeam using AFM

Micro-Raman Spectroscopy Analysis of Residual Stress in Polysilicon MEMS Resonators

Microbridge testing of Young's modulus and residual stress of nickel film electroplated on silicon wafer