Abstract:The unsatisfactory high-temperature performance of commonly used silicon carbide (SiC)-based ceramics calls for a novel approach for their reinforcement. We present the in situ preparation of a SiC-based composite with uniformly dispersed titanium boride (TiB2) particles using titanium carbide and boron carbide as raw materials. Notably, the uniform incorporation of 25 wt%TiB2 results in the SiC–TiB2 composite with excellent tribological and self-lubricating properties at high temperatures. The SiC–TiB2 composite shows a friction coefficient of 0.20 and a specific wear rate of 5.77 × 108 mm3/(N mm), which are 4.75 times and ~ 5.2 times lower than that of the bare SiC ceramic at 1000 °C, respectively. The wear mechanism of a self-mated couple of the SiC–TiB2 composite is unraveled to be the tribo-oxidization. Since intimate contact exists between the oxidizing layer and the transitional layer of the fractured surface, the friction surface possessing plastic deformation properties may transit from brittle to plastic or elastic. The "Pin Effect" exhibited by TiB2 particles in the SiC–TiB2 composite deflects the crack propagation route. Meanwhile, a change in stress distribution, a decrease in the stress intensity of slight crack frontier, and an increase in "the threshold value" of crack propagation occur. The type (I + II) and type (I + III) complex cracks in fracture mechanics propagate non-flatly in the wearing process of the self-mated couple of the SiC–TiB2 composite. Besides, a fine yield deformation zone exists on the crack tip. Consequently, the "threshold value" of crack propagation fluctuates dynamically between "upper bound value" and "lower bound value" following the change in the valid length of actual crack propagation, thus delaying the fracture of the SiC–TiB2 composite.

Wear mechanisms of pairs of Si3N4-based and Ti(CN)-based ceramic with 1Cr18Ni9Ti stainless steel under dry-friction condition

Analysis on Wear Properties and Impact Factors for Si3N4 Ceramic Mated with Chilled Cast Iron

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Tribological Characteristics of Silicon Nitride-chilled Cast Iron with Oil-less Lubrication

Wear mechanisms of Ti(C, N) ceramic in sliding contact with stainless steel

Friction and Wear of Si3N4 Ceramic/stainless Steel Sliding Contacts in Dry and Lubricated Conditions

Tribological Characteristics of Si3N4 Ceramic Sliding on Stainless Steel

Wear Behavior of Si3N4 Ceramic Cutting Tool Material Against Stainless Steel in Dry and Water-Lubricated Conditions

Wear Behavior of Al 2 O 3 -Ticn Composite Ceramic Sliding on Stainless Steel

Cutting performances and their failure mechanisms of ceramic tools for cutting stainless steel

Effects of Lubricants on Friction and Wear of Ti(Cn)/1045 Steel Sliding Pairs

In-situ friction and wear study of SiCα/SiCβ and Al2O3-TiC-Co composite ceramics

In situ preparation of a SiC–TiB2 composite and its wear fracture mechanism at high temperatures

Friction and Wear Properties of CrSiCN/SiC Tribopairs in Water Lubrication

Synergistic effect of surface textures and DLC coatings for enhancing friction and wear performances of Si3N4/TiC ceramic

Understanding wear mechanisms of TiSiCN/Zr(C)N coatings at elevated temperatures

Friction and wear properties of CrSiCN coatings with low carbon content as sliding against SiC and steel balls in water

Investigation on the tribological properties of ceramics rubbing against stainless steel at high temperature

Tribological performance of DLC-coated ceramics against cemented carbide under dry sliding conditions

Research on Tribology Property of Si-3N-4 Ceramic and Chilled Iron under Oil-Less Lubrication

Tribological Behavior of Liquid Phase Sintered SiC Ceramics Under Dry Condition