Preparation And Investigation Of Cu Doped (Pr0.5nd0.5)(0.7)Ca0.3cro3-Delta Ceramic Interconnect Materials

qing wen gu,yong hong chen,Dong Tian,xiao yong lu,yan zhi ding,Bin Lin

DOI: https://doi.org/10.4028/www.scientific.net/AMM.448-453.2950

2014-01-01

Applied Mechanics and Materials

Abstract:(Pr0.3Nd0.5)(0.7)Ca0.3Cr1-xCuxO3-delta(PNCCCx x=0, 0.5, 0.1, 0.15, 0.2) interconnect material and electro-lyte powders of Sm0.2Ce0.8O1.9 (SDC) were synthesized by citric acid nitrates self-propagating combustion method. The phase and microstructure of the sintering samples were investigated by X-ray diffraction and scanning electr-on microscope, respectively. The electrical conductivity of the samples were measured by four-probe technique. The results indicated that there is no new-phase were detected after co-firing between Cu-doping PNCC and SDC at 1350 degrees C for 5 h. In air or H-2 atmosphere, the conductivity of the sintering ceramics increasing with temperature, as well as the Cu-doped contents. At 800 degrees C, the conductivity for PNCCC0.05 reached 37.54S/cm in air, and the maximum of PNCCC/SDC reached 44.52 S/cm in air 30.68 S/cm in H-2, respectively. The average thermal expansion coefficient of the series ceramics is between 10.4x10(-6) K-1 to 10.8x10(-6) K-1 at the RT-1000 degrees C, which is close to that of the SDC electrolyte. Our results indicate that the PNCCC compounds is a very promising interconnect material for intermediate solid oxide fuel cells.