Preparation and Electrical Properties of Novel Sm_(0.9)Sr_(0.1)Al_(1-x)Cr_xO_(3-δ) Mixed Conducting Ceramics

Yanqiu Chu

2011-01-01

Abstract:A series of Sm0.9Sr0.1Al1-xCrxO3-δ(SSAC,x = 0-0.4) oxygen anion-electron mixed conducting ceramics were prepared by organic-gel process and subsequent high-temperature sintering.Thermal decomposition and phase evolution processes of gel precur-sors as well as crystal structure,micromorphology and electrical properties of sintered samples were investigated by thermogravimet-ric-differential thermal analysis,X-ray diffraction,scanning electron microscopy,and direct current four-wire technique.Results re-veal that well-crystallized Sm0.9Sr0.1Al1-xCrxO3-δ nanopowders with an orthorhombic perovskite structure can be obtained by calcining the gel precursors at 900 ℃ for 5 h.Conductivities of SSAC ceramics are dominated by p-type conduction and conduction behavior conforms to the adiabatic small polaron hopping transport mechanism.Both electrical conductivity and relative density of Sm0.9Sr0.1Al0.6Cr0.4O3-δ ceramics increase initially and then decrease with increasing sintering temperature,and the sample sintered at 1 550 ℃ for 10 h has the highest electrical conductivity and relative density among all the samples.The conductivities and lattice constants of the SSAC ceramics with different compositions exhibit the same dependence on Cr dosage and their values first increase and then decrease with increasing Cr dosage,and finally begin to increase again as x is more than 0.2,while the dependence of corre-sponding apparent activation energies on Cr dosage is just the opposite.