Preparation and Application of La1-xSrxCoO3-delta Conductive Ceramics
He Qing,Chen Lawson,Shen Qianhong,Zhang Lingjie,Wu Xinhe,Mu Chengfa,Fan Xianping,Yang Hui
2013-01-01
Rare Metal Materials and Engineering
Abstract:La1-xSrxCoO3-delta conductive ceramic powders with different strontium content (x=0.1 similar to 0.7) were synthesized with a solid state method and a sol-gel method. Both the structure and properties of the LSCO samples were investigated, and a new Ag/LSCO material was designed during the exploration of its applications in the environmentally friendly electrical contact materials. Compared with LSCO particles prepared by the solid state method, samples prepared by the sol-gel method are spherical and with smaller particle size (approximately 50 nm), and they generally also have good electrical conductivity (10(3) S.cm(-1)). More importantly, LSCO particles prepared by the sol-gel method can partially be decomposed in the temperature range of 700 similar to 950 degrees C, while giving off O-2. The emitted oxygen can help to prevent welding and blow out the arc when it occurs in the working process of electrical contact materials, effectively reducing the destruction of the arc on the Ag matrix. The similar thermodynamic behaviors occur in CdO qualified Ag/CdO as one of the best electrical contact material, but they can not be found in the samples prepared by the solid state method. Consequently, LSCO powders prepared by the sol-gel method are more worthy of being chosen as reinforcements in the designing of silver based eco-friendly electrical contact materials.