Abstract:Self-standing iron nanowires were fabricated at the apex of a tungsten needle tip by electron beam induced deposition. This sharp needle tip which adhered to the nanowire can be moved with a stepping motor and piezo-driving device, and was attached inside a specially designed transmission electron microscope specimen holder. A copper conductor substrate, with which the approaching nanowires will build up a closed electric circuit, was set on the holder. The tungsten needle tip accompanied with the EBICVD nanowires made contact with the substrate and then a voltage was applied between the two electrodes. Resistivity values of the examined nanowires, by a devised Lock-in-Amplifier circuit, range from 0.1 m to 103 m. Our investigation might have implications in the fabrication and characterization of nano-electronics device. Precursor with phenanthrene (C4H10) was used and the deposition experiment was done using a scanning electron microscope at room temperature. It was found that the surface structure at the top of the nanorod, such as a small protrusion within only several nanometers scale, has significant influence on the field emission property. An emission current of several tens of nano-ampere flowing through this nanorod could induce resistance heating. In several minutes, this thermal energy could transform the original amorphous carbon into a graphite-like structure embedded with fullerenes. The turn-on voltage of the graphite-like nanorod was about 11 V less than that of the original amorphous case.

Copper Nanowires Preparation and Field Electron Emission Properties

Field Emission From Crystalline Copper Sulphide Nanowire Arrays

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

Preparation of Aligned Cu2s Nanowire Arrays and Their Field Emission Properties

Preparation of Cuo Nanowire Field Emitter Arrays by Thermal Oxidation in Water Vapor Containing Environments and Their Field Emission Properties

The Influence of Copper Substrate Treatment on the Growth of Cu/sub 2/S Nanowires Arrays and Their Field Emission Characteristics

Field Emission From Short And Stubby Vertically Aligned Carbon Nanotubes

Field Electron Emission from Cupric Oxide-Nanobelt Films

G030084 Fabrication of High Density Cu Nanowire Array by Template Method and Its Evaluation

J212025 Fabrication of Nanowire Surface Fastener on Flexible Substrate and Its Electrical and Mechanical Properties

Enhanced field emission and patterned emitter device fabrication of metal-tetracyanoquinodimethane nanowires array

Resistivity and Field Electron Emission of Nanowires Formed by Electron Beam Induced Chemical Vapor Deposition

A Novel Application of the CuI Thin Film for Preparing Thin Copper Nanowires

P-type Electrical, Photoconductive, and Anomalous Ferromagnetic Properties of Cu2O Nanowires

Field-Emission Properties of Nanostructured Wo3 Arrays Fabricated Using Tungsten Hot-Filament Chemical Vapor Deposition

Cuprite Nanowires by Electrodeposition from Lyotropic Reverse Hexagonal Liquid Crystalline Phase

Large-scale Growth of Copper Oxide Nanowires on Various Copper Substrates

Electrochemical Synthesis of Copper Nanowires

Effect of Structural Parameter on Field Emission Properties of Semiconducting Copper Sulphide Nanowire Films

The Electrochemical Response of Single Crystalline Copper Nanowires to Atmospheric Air and Aqueous Solution

Thermal expansion of Cu nanowire arrays