Abstract:Metal oxide nanowires (NWs) can be easily grown by the thermal oxidation method, but the low adhesion between the NWs and the substrate restricts their practical applications in functional devices. In this work, the conventional hotplate technique is simply modified by introducing one or two stainless steel plates to supply a more stable oxidation environment, which is found to be beneficial to the growth and adhesion of CuO NWs on the Cu substrate. In detail, the Cu foils were heated on the hotplate directly, on one plate over the hotplate, and between two plates over the hotplate at 400 °C in ambient condition. It is found that the NWs obtained between two plates exhibit large length and diameter with moderate density. The sufficient activated oxygen, stable temperature, and proper temperature gradient configuration caused by the two plates accelerate the formation of CuO NWs, and result in the longest NWs with enhanced adhesion. The grain-boundary diffusion and Kirkendall effect are proposed to explain the mechanism of NWs growth and the formation of cracks. The NWs obtained between two plates also showed the best field emission properties, with lowest turn-on field (5.31 V μm(-1)) and threshold field (9.8 V μm(-1)). Excellent field emission properties and enhanced NW-substrate adhesion indicate that these NW arrays could be potentially used as the cathode of field emission displays.

The Influence of Copper Substrate Treatment on the Growth of Cu/sub 2/S Nanowires Arrays and Their Field Emission Characteristics

Preparation of Aligned Cu2s Nanowire Arrays and Their Field Emission Properties

Large-scale Growth of Copper Oxide Nanowires on Various Copper Substrates

Oxide-assisted nucleation and growth of copper sulphide nanowire arrays

Synthesis of Copper Nanowires on the Substrates in Aqueous Solution

Growth of Crystalline Cu<sub>2</sub>S Nanowire Arrays on Copper Surface: Effect of Copper Surface Structure, Reagent Gas Composition, and Reaction Temperature

Copper Nanowires Preparation and Field Electron Emission Properties

The Crystal Structure And Growth Direction Of Cu2s Nanowire Arrays Fabricated On A Copper Surface

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

Preparation and characterization of single crystal CuS nanowires using electro-deposition method

Effect of Structural Parameter on Field Emission Properties of Semiconducting Copper Sulphide Nanowire Films

J212025 Fabrication of Nanowire Surface Fastener on Flexible Substrate and Its Electrical and Mechanical Properties

Enhanced Adhesion and Field Emission of CuO Nanowires Synthesized by Simply Modified Thermal Oxidation Technique.

Fabrication and characterization of patterned of copper nanowire arrays

CuO Nanowire Arrays: Preparation, Characterization and Field Emission Properties

Growth Behaviour of Straight Crystalline Copper Sulphide Nanowires

Field Emission From Crystalline Copper Sulphide Nanowire Arrays

Growth of Aligned Cu2s Nanowire Arrays with Aao Template and Their Field-Emission Properties

Self-Assembled Zns Nanowire Arrays: Synthesis, in Situ Cu Doping and Field Emission

The Effect of Substrate on Magnetic Properties of Co/Cu Multilayer Nanowire Arrays