Abstract:Synthesis and characterization of noble metal nanowires have been a popular topic in the field of microelectronic devices and catalysts. Nanotwinned copper nanowires (nt-CuNWs) possess high mechanical strength, excellent electromigration resistance and low electrical resistivity, which have been considered as a promising interconnect material in ultra-large scale integrated circuits (ICs). Here, we deposited nt-CuNWs in two different anodic aluminum oxide (AAO) templates with respective pore sizes of 70 nm and 35 nm pore by pulse electrodeposition. The influence of thermal treatment on the Cu seed layer deposited on AAO membranes prior to electrodeposition is investigated. Both coarse and thin nt-CuNWs mainly grew in crystallographic direction with (111) texture coefficients (TC (111) ) > 2.5, and an aspect ratio (AR) > 100 according to x-ray diffraction analysis. An addition of gelatin (14 ppm) in the copper sulfate electrolyte is found to suppress the growth of (220)-oriented Cu grains in the AAO by forming copper nanowires with large TC (111) > 2.65 and high-density nanotwin structure. This study provides a simple route to tailoring microstructure and physical properties of nanoscale copper wires, which is beneficial for the interconnect technology development in semiconductor IC devices.

Growth of Aligned Cu2s Nanowire Arrays with Aao Template and Their Field-Emission Properties

Preparation of Aligned Cu2s Nanowire Arrays and Their Field Emission Properties

J212025 Fabrication of Nanowire Surface Fastener on Flexible Substrate and Its Electrical and Mechanical Properties

G030084 Fabrication of High Density Cu Nanowire Array by Template Method and Its Evaluation

Stress-Induced Growth of Well-Aligned Cu2o Nanowire Arrays and Their Photovoltaic Effect

Preparation and Characterization of CdS Nanowire Arrays by Dc Electrodeposit in Porous Anodic Aluminum Oxide Templates

Field Emission From Crystalline Copper Sulphide Nanowire Arrays

Self-Assembled Zns Nanowire Arrays: Synthesis, in Situ Cu Doping and Field Emission

The Control of the Growth Orientations of Electrodeposited Single-Crystal Nanowire Arrays: a Case Study for Hexagonal CdS.

Oxide-assisted nucleation and growth of copper sulphide nanowire arrays

Diameter- and current-density-dependent growth orientation of hexagonal CdSe nanowire arrays via electrodeposition.

Template-Free Growth of Vertically Aligned Cds Nanowire Array Exhibiting Good Field Emission Property

Field Emission Of Large-Area And Graphitized Carbon Nanotube Array On Anodic Aluminum Oxide Template

Synthesis and I-V Properties of Aligned Copper Nanowires.

Field-Emission Properties of Nanostructured Wo3 Arrays Fabricated Using Tungsten Hot-Filament Chemical Vapor Deposition

Vertically Aligned Tin-Doped Indium Oxide Nanowire Arrays: Epitaxial Growth And Electron Field Emission Properties

Synthesis and Field-Emission Properties of Aligned MoO3 Nanowires

Patterned Growth of AlN Nanowires and Investigation on Their Field Emission Properties

P1–8: Low Temperature Gowth and Field Emission Properties of Patterned Tungsten Oxide Nanowire Arrays by Using Cceramic Template

Control of Crystallographic Growth Orientation and Twinning Structure in Copper Nanowires by Template-Assisted Electrodeposition

P1-8: Low temperature gowth and field emission properties of patterned tungsten oxide nanowire arrays by using cceramic template