Abstract:A vertically aligned Pd nanowire array was successfully fabricated on an Au/Ti substrate using an anodic aluminum oxide (AAO) template by a direct voltage electrodeposition method at room temperature using diluted neutral electrolyte. The fabrication of Pd nanowires was controlled by analyzing the current–time transient during electrodeposition using potentiostat. The AAO template and the Pd nanowires were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) methods and X-Ray diffraction (XRD). It was observed that the Pd nanowire array was standing freely on an Au-coated Ti substrate after removing the AAO template in a relatively large area of about 5 cm2, approximately 50 nm in diameter and 2.5 μm in length with a high aspect ratio. The nucleation rate and the number of atoms in the critical nucleus were determined from the analysis of current transients. Pd nuclei density was calculated as 3.55 × 108 cm−2. Usage of diluted neutral electrolyte enables slower growing of Pd nanowires owing to increase in the electrodeposition potential and thus obtained Pd nanowires have higher crystallinity with lower dislocations. In fact, this high crystallinity of Pd nanowires provides them positive effect for sensor performances especially.A vertically aligned Pd nanowire array was successfully fabricated on an Au/Ti substrate using an anodic aluminum oxide (AAO) template by a direct voltage electrodeposition method at room temperature using diluted neutral electrolyte. The fabrication of Pd nanowires was controlled by analyzing the current–time transient during electrodeposition using potentiostat. The AAO template and the Pd nanowires were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) methods and X-Ray diffraction (XRD). It was observed that the Pd nanowire array was standing freely on an Au-coated Ti substrate after removing the AAO template in a relatively large area of about 5 cm2, approximately 50 nm in diameter and 2.5 μm in length with a high aspect ratio. The nucleation rate and the number of atoms in the critical nucleus were determined from the analysis of current transients. Pd nuclei density was calculated as 3.55 × 108 cm−2. Usage of diluted neutral electrolyte enables slower growing of Pd nanowires owing to increase in the electrodeposition potential and thus obtained Pd nanowires have higher crystallinity with lower dislocations. In fact, this high crystallinity of Pd nanowires provides them positive effect for sensor performances especially.

Synthesis and I-V Properties of Aligned Copper Nanowires.

Control of Crystallographic Growth Orientation and Twinning Structure in Copper Nanowires by Template-Assisted Electrodeposition

G030084 Fabrication of High Density Cu Nanowire Array by Template Method and Its Evaluation

J212025 Fabrication of Nanowire Surface Fastener on Flexible Substrate and Its Electrical and Mechanical Properties

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

Copper-Based Nanowire Materials: Templated Syntheses, Characterizations, and Applications

A Simple Route to Aligned AlN Nanowires

Fabrication and Electrical Properties of a Cu–tetracyanoquinodimethane Nanowire Array in a Porous Anodic Alumina Template

Nanowire Arrays Electrodeposited from Liquid Crystalline Phases

Growth of Aligned Cu2s Nanowire Arrays with Aao Template and Their Field-Emission Properties

Fabrication of Anodic Aluminum Oxide Template and Cu Nanowire Surface Fastener

Electrochemical Synthesis of Copper Nanowires

Synthesis and Superconductivity of Electrochemically Grown Single-Crystal Aluminum Nanowires

Preparation of Aligned Cu2s Nanowire Arrays and Their Field Emission Properties

Nanoscale Twinned Copper Nanowire Formation by Direct Electrodeposition.

Controllable Template Synthesis of Ni/Cu Nanocable and Ni Nanotube Arrays: a One-Step Coelectrodeposition and Electrochemical Etching Method.

A technique for controlling the alignment of silver nanowires with an electric field

Structure and magnetic property of Ni-Cu alloy nanowires electrodeposited into the pores of anodic alumina membranes

Fabrication of vertically aligned Pd nanowire array in AAO template by electrodeposition using neutral electrolyte

Synthesis and Characterization of Single-Crystalline Alumina Nanowires

Electrochemical Synthesis of Metal and Semimetal Nanotube-Nanowire Heterojunctions and Their Electronic Transport Properties.