Effect of CO2 partial pressure on the corrosion in flow and transport lines under the erosion action:A case study from the Xushen-6 Gas Station in the Daqing Oil Field

Cui Yue,Lan Huiqing,He Renyang,Bai Xiaoxu,Huang Hui

DOI: https://doi.org/10.3787/j.issn.1000-0976.2013.02.025

2013-01-01

Abstract:The content of CO2 and water is rather high in the gathering and transportation lines in some oil and gas fields. Moreover, the operating pressure needs to be enhanced at the gathering and transmission stations to improve the flow rate in the lines. This leads to the increasingly serious result of the CO2 dominated corrosion in the lines. Therefore, to master the changing law of CO2 dominated corrosion induced by flow field is of great significance to corrosion prevention & control and regular inspection. In view of this, a case study was made of a pipeline at the Xushen-6 Gas Station in the Daqing Oil Field. First, based on the Norsok corrosion model, the effect of CO2 partial pressure was predicted on the corrosion rate at the inner side wall of this pipeline. Then, the computational fluid dynamics (CFD) module was used to analyze the flow field in the pipeline; and in combination with the pipe wall thickness, it is disclosed that how the partial CO2 pressure influences the internal corrosion in a pipeline under the erosion action. In a pipe line, erosion accelerates the partial CO2 corrosion distinctly in the specific parts such as tees or elbows with a violent change of turbulent flow, the kinetic energy of which increases to the maximum value of 75 m2/s2; flow patterns and velocity exacerbate the C2 corrosion evenly at the inner wall of the pipe. With the CO2 partial pressure increasing, the average CO2 corrosion rate sharply rises in the pipe line; but when the C2 content reaches a saturation value in a gas-water transport line, the C2 corrosion will tend towards stability and the expected C 2 corrosion rate rises on the whole. During the severe C2 corrosion interval (0. 02 - 0. 20 MPa), the C2 corrosion level enlarges linearly with the increase of C2 partial pressure, subsequently, the maximum of the corrosion rate holds a value of 0. 75 mm/year and the minimum of the corrosion rate is kept at 0. 62 mm/year. This study will provide a reference for predicting the life span of the key parts of a pipeline and also help improve the efficiency of corrosion prevention & control and regular inspection of pipelines.