Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Solvothermal synthesis of gamma aluminas and their structural evolution

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Morphology Controllable Synthesis Of Gamma-Alumina Nanostructures Via An Ionic Liquid-Assisted Hydrothermal Route

Sol-Gel Synthesis of Alumina Using Inorganic Salt Precursor

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Facile Synthesis of Hierarchical Flower-Like Γ-Alooh Films Via Hydrothermal Route on Quartz Surface

Hydrothermal synthesis of microscale boehmite and gamma nanoleaves alumina

A new route to synthesis of γ-alumina nanorods

Surface and pore structure of alumina derived from xerogel/aerogel

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Synthesis of Morphology-Controlled Mesoporous Transition Aluminas Derived from the Decomposition of Alumina Hydrates

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Clean Synthesis of Hierarchically Structured Boehmite and Γ-Alumina with a Flower-Like Morphology

Morphology Evolution in Hydrothermal Synthesis of Mesoporous Alumina

Preparation of Pseudo-Boehmite and Gamma-Al2o3 by Polyaluminum Chloride Ii -Surfactant Influences

Synthesis of Mesoporous gamma-Al2O3 Templated with Rosin-Based Quaternary Ammonium Salt by Ammonia Precipitation

Catanionic-Surfactant Templated Synthesis Of Organized Mesoporous Gamma-Alumina By Double Hydrolysis Method

Synthesis of Mesoporous Γ-Al2o3 with Hydrangea-Like by the Ethanol-Thermal Method

Synthesis of Flower-Like Boehmite (Γ-Alooh) Via a One-Step Ionic Liquid-Assisted Hydrothermal Route

New sol-gel route using inorganic salt for synthesizing Al2O3 nanopowders

Morphology-controlled Synthesis of Γ-Al2o3 with Large Mesopores Through Combustion of Aluminum Carboxylate Salts