Abstract:Highly dispersed CeO2 on carbon nanotubes (CNTs) is successfully prepared by a pyridine-thermal route for selective catalytic reduction (SCR) of NO with NH3. This catalyst is mainly characterized by the techniques of X-ray diffraction (XRD), transmission electron microscopy (TEM), temperature-programmed reduction by hydrogen (H-2-TPR), temperature-programmed desorption of ammonia (NH3-TPD) and X-ray photoelectron spectroscopy (XPS). The results of the XRD, TEM and TPR analysis show that the CeO2 particles on the CNTs are highly dispersed with a strong interaction between the particles and the CNTs. The NH3-TPD profiles indicate that this catalyst exhibits abundant strong acid sites. Furthermore, the O 1s XPS spectra show that the O-alpha/(O-alpha + O-beta) ratio of this catalyst is very high, which can result in more surface oxygen vacancies and therefore favor the NH3-SCR reaction. Compared with the catalysts prepared by impregnation or physical mixture methods, the catalyst prepared by the pyridine-thermal route presents the best NH3-SCR activity in the temperature range of 150-380 degrees C as well as favourable stability and good SO2 or H2O resistance. More than 90% of NO can be removed in the range of 250-370 degrees C with a desirable N-2 selectivity. Moreover, the NO conversion can be kept at about 97% with the presence of SO2 or H2O at 300 degrees C. In addition, this catalyst shows a high catalytic activity with a NO conversion remaining constant at ca. 98% during a 16 h continuous run duration at 300 degrees C. Highly dispersed CeO2 on the CNTs as well as the strong interaction between the particles and the CNTs, the large amounts of strong acid sites and the high O-alpha/(O-alpha + O-beta) ratio could be ascribed to the excellent NH3-SCR performance of the catalyst prepared by the pyridine-thermal route.

Highly Dispersed Ceo2 on Carbon Nanotubes for Selective Catalytic Reduction of No with Nh3

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

MnOx-CeOx/CNTs pyridine-thermally prepared via a novel in situ deposition strategy for selective catalytic reduction of NO with NH3

In Situ Supported Mnox-Ceox On Carbon Nanotubes For The Low-Temperature Selective Catalytic Reduction Of No With Nh3

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Selective Catalytic Reduction of No over Carbon Nanotubes Supported Ceo2

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Bimetallic Cerium–copper Nanoparticles Embedded in Ordered Mesoporous Carbons As Effective Catalysts for the Selective Catalytic Reduction of NO with NH3

A novel CNTs functionalized CeO2/CNTs–GAC catalyst with high NO conversion and SO2 tolerance for low temperature selective catalytic reduction of NO by NH3

Enhanced Catalytic Activity for Selective Catalytic Reduction of NO over Titanium Nanotube-Confined CeO2 Catalyst

The activity and characterization of CeO2-TiO2 catalysts prepared by the sol-gel method for selective catalytic reduction of NO with NH3.

CuOx and WOx modified CeO2-TiO2 with various morphologies for the selective catalytic reduction of NOx with NH3

Preparation and characterization of CeO2/TiO2 catalysts for selective catalytic reduction of NO with NH3

A superior CeO2 @TiO2 catalyst with high dispersion of CeO2 for selective catalytic reduction of NOx with NH3

Selective catalytic reduction of NO<sub>x</sub> with NH<sub>3</sub> over a novel Co-Ce-Ti catalyst

A Ce–Cu–Ti oxide catalyst for the selective catalytic reduction of NO with NH3

Low-temperature Selective Catalytic Reduction of NO with NH3 over Nanoflaky MnOx on Carbon Nanotubes in Situ Prepared Via a Chemical Bath Deposition Route

Activity and Characterization of Ce–Mo–Ti Mixed Oxide Catalysts Prepared by a Homogeneous Precipitation Method for Selective Catalytic Reduction of NO with NH3

High-performance CeO2/halloysite Hierarchical Catalysts with Promotional Redox Property and Acidity for the Selective Catalytic Reduction of NO with NH3

The Superior Performance of Nb-modified Cu-Ce-Ti Mixed Oxides for the Selective Catalytic Reduction of NO with NH3 at Low Temperature

Ce-O-P Material Supported CeO2 Catalysts: A Novel Catalyst for Selective Catalytic Reduction of NO with NH3 at Low Temperature