Abstract:Highly dispersed CeO2 on carbon nanotubes (CNTs) is successfully prepared by a pyridine-thermal route for selective catalytic reduction (SCR) of NO with NH3. This catalyst is mainly characterized by the techniques of X-ray diffraction (XRD), transmission electron microscopy (TEM), temperature-programmed reduction by hydrogen (H-2-TPR), temperature-programmed desorption of ammonia (NH3-TPD) and X-ray photoelectron spectroscopy (XPS). The results of the XRD, TEM and TPR analysis show that the CeO2 particles on the CNTs are highly dispersed with a strong interaction between the particles and the CNTs. The NH3-TPD profiles indicate that this catalyst exhibits abundant strong acid sites. Furthermore, the O 1s XPS spectra show that the O-alpha/(O-alpha + O-beta) ratio of this catalyst is very high, which can result in more surface oxygen vacancies and therefore favor the NH3-SCR reaction. Compared with the catalysts prepared by impregnation or physical mixture methods, the catalyst prepared by the pyridine-thermal route presents the best NH3-SCR activity in the temperature range of 150-380 degrees C as well as favourable stability and good SO2 or H2O resistance. More than 90% of NO can be removed in the range of 250-370 degrees C with a desirable N-2 selectivity. Moreover, the NO conversion can be kept at about 97% with the presence of SO2 or H2O at 300 degrees C. In addition, this catalyst shows a high catalytic activity with a NO conversion remaining constant at ca. 98% during a 16 h continuous run duration at 300 degrees C. Highly dispersed CeO2 on the CNTs as well as the strong interaction between the particles and the CNTs, the large amounts of strong acid sites and the high O-alpha/(O-alpha + O-beta) ratio could be ascribed to the excellent NH3-SCR performance of the catalyst prepared by the pyridine-thermal route.

A novel CNTs functionalized CeO2/CNTs–GAC catalyst with high NO conversion and SO2 tolerance for low temperature selective catalytic reduction of NO by NH3

Highly Dispersed Ceo2 on Carbon Nanotubes for Selective Catalytic Reduction of No with Nh3

Low-Temperature Scr Of No With Nh3 Over Ceo2 Supported On Modified Activated Carbon Fibers

Copper Doping Promotion on Ce/CAC-CNT Catalysts with High Sulfur Dioxide Tolerance for Low-Temperature NH 3 –SCR

Improvement in Activity and Alkali Resistance of a Novel V-Ce(SO4)2/Ti Catalyst for Selective Catalytic Reduction of NO with NH3

MnOx-CeOx/CNTs pyridine-thermally prepared via a novel in situ deposition strategy for selective catalytic reduction of NO with NH3

Mn-Ce Oxide Nanoparticles Supported on Nitrogen-Doped Graphene for Low-Temperature Catalytic Reduction of NOx: De-Nitration Characteristics and Kinetics

CeO2 Nanoparticle-Loaded MnO2 Nanoflowers for Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

In Situ Supported Mnox-Ceox On Carbon Nanotubes For The Low-Temperature Selective Catalytic Reduction Of No With Nh3

Simultaneous removal of NO x and SO 2 by low-temperature selective catalytic reduction over modified activated carbon catalysts

Graphene Based Mesoporous Manganese-Cerium Oxides Catalysts:Preparation and Low-temperature Catalytic Reduction of NO

Preparation and characterization of CeO2/TiO2 catalysts for selective catalytic reduction of NO with NH3

Low-Temperature Scr of No with Nh3 over Activated Semi-Coke Composite-Supported Rare Earth Oxides

Nitrogen-Doped Pitch-Based Activated Carbon Fibers with Multi-Dimensional Metal Nanoparticle Distribution for the Effective Removal of NO

The Superior Performance of Nb-modified Cu-Ce-Ti Mixed Oxides for the Selective Catalytic Reduction of NO with NH3 at Low Temperature

Low-temperature selective catalytic reduction of NO on CeO2-CuO/Al2O3 catalysts prepared by different methods

The activity and characterization of CeO2-TiO2 catalysts prepared by the sol-gel method for selective catalytic reduction of NO with NH3.

Low-temperature selective catalytic reduction of NO with NH3 over Mn–Ce–Ox/TiO2: a comparison between catalyst preparation methods

A Ce–Cu–Ti oxide catalyst for the selective catalytic reduction of NO with NH3

Graphitic carbon nitride (g-C3N4) as a super support for Mn–Ce based NH3-SCR catalyst: Improvement of catalytic performance and H2O/SO2 tolerance for NO removal

Low-temperature Selective Catalytic Reduction of NO with NH3 over Nanoflaky MnOx on Carbon Nanotubes in Situ Prepared Via a Chemical Bath Deposition Route