Enhanced Ductility of B4C/Al Composites by Controlling Thickness of Interfacial Oxide Layer Through High Temperature Oxidation of B4C Particles
Longtao Jiang,Wei Xue,Pengchao Kang,Zhenlong Chao,Huimin Han,Runwei Zhang,Shanqi Du,Binzhuo Han,Qiqi Zhao,Gaohui Wu
DOI: https://doi.org/10.1016/j.jallcom.2022.168486
IF: 6.2
2023-01-01
Journal of Alloys and Compounds
Abstract:Pre-oxidizing of the B4C particles can regulate the thickness of the interfacial oxide layer between the B4C particles and the Al alloy matrix in the B4C/Al composites by adjusting the oxidation temperature and time. This paper studied the effect of oxidation temperature and time on the oxide layer of the B4C particles, which was oxidized at 500 degrees C similar to 650 degrees C in air quantitatively. Taking the pre-oxidized B4C particles as raw reinforcements, the B4C/Al composites with a volume fraction of 15% were prepared by hot pressed sin-tering method, and the interfacial microstructure and tensile properties of the composites were discussed. The results show that the amorphous oxide layers with different average thickness are produced at the interface of the composites, which prepared by the B4C particles through different oxidation processes, and the average thickness of the oxide layer has a great influence on the fracture elongation of the B4C/Al composites. When the average thickness of the oxide layer is 9.6 nm, the composites show the highest value of the fracture elongation (4.2%), 50% and 147% higher than that in the composites with the average thickness of 0 and 37.6 nm. By designing the thickness of the interfacial oxide layer, it is expected to realize the regulation of the tensile properties of the B4C/Al composites. \(c) 2022 Elsevier B.V. All rights reserved.