Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

High-Temperature Oxidation Resistance of ZrB2-SiC Ceramic Composites Prepared by Reactive Hot Pressing

High temperature oxidation resistance of hot-pressed h-BN/ZrO 2 composites

Microstructure, Mechanical Properties and Oxidation Behavior of Reactive Hot-Pressed (Zr,Ti)B2-SiC-ZrC Composites

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Oxidation response of ZrB2–SiC–ZrC composites prepared by spark plasma sintering

Effect of boronizing treatment on the oxidation resistance of Zr2(AlSi)4C5/SiC composite

Characterization of hot‐pressed ZrC–TiC composites

Oxidation Behavior of Sic Platelet-Reinforced Zrb2 Ceramic Matrix Composites

Preparation of Mo25ZrB2 Cermet by Hot Pressing Sintering and Its Static Oxidation Behavior

High temperature oxidation resistance of Y2O3 modified ZrB2-SiC coating for carbon/carbon composites

Phase stability, hardness and oxidation behaviour of spark plasma sintered ZrB2-SiC-Si3N4 composites

Study on the oxidation resistance of carbon ceramic composite

Isothermal Oxidation of Zr2[Al(Si)]4C5–SiC Composites at 1000–1300°C in Air

Preoxidation and Crack-Healing Behavior of ZrB<sub>2</sub>-SiC Ceramic Composite

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Enhanced Oxidation Resistance of ZrB2‐SiC‐WC Composite Below 1800 °C

Effect of Lu2O3 addition on the oxidation behavior of SiC-ZrB2 composite coating at 1500 °C: Experimental and theoretical study