Abstract:ZrB2-SiC-Zr2Al4C5 multi-phase ceramics with uniform structure and high density were successfully prepared through the introduction of in situ synthesized Zr2Al4C5 into ZrB2-SiC ceramic via SPS at 1800 °C. A systematic analysis and discussion of the experimental results and proposed mechanisms were carried out to demonstrate the composition-dependent sintering properties, mechanical properties and oxidation behavior. The results showed that the in situ synthesized Zr2Al4C5 could be evenly distributed in the ZrB2-SiC ceramic matrix and inhibited the growth of ZrB2 grains, which played a positive role in the sintering densification of the composite ceramics. With increasing Zr2Al4C5 content, the Vickers hardness and Young's modulus of composite ceramics gradually decreased. The fracture toughness showed a trend that first increased and then decreased, and was increased by about 30% compared with ZrB2-SiC ceramics. The major phases resulting from the oxidation of samples were ZrO2, ZrSiO4, aluminosilicate and SiO2 glass. With increasing Zr2Al4C5 content, the oxidative weight showed a trend that first increased then decreased; the composite ceramic with 30 vol.% Zr2Al4C5 showed the smallest oxidative weight gain. We believe that the presence of Zr2Al4C5 results in the formation of Al2O3 during the oxidation process, subsequently resulting in a lowering of the viscosity of the glassy silica scale, which in turn intensifies the oxidation of the composite ceramics. This would also increase oxygen permeation through the scale, adversely affecting the oxidation resistance of the composites with high Zr2Al4C5 content.

Study on the oxidation resistance of carbon ceramic composite

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites

High-Temperature Oxidation Resistance of ZrB2-SiC Ceramic Composites Prepared by Reactive Hot Pressing

Study on the oxidation mechanism of Al-SiC composite at elevated temperature

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

Multi-composition Coating for Oxidation Protection of Modified Carbon-Bonded Carbon Fiber Composites

Oxidation Behavior of Carbon Fibers in Ceramizable Phenolic Resin Matrix Composites at Elevated Temperatures

High temperature flexural strength, microstructure, phase evolution and anti-oxidation mechanism of Al-coated carbon fiber/boron phenolic resin ceramizable composite modified with TiB2 and B4C

High Temperature Oxidation Resistance Of Ti3sic2 In Air And Low Oxygen Atmosphere

High temperature oxidation behavior and mechanism of SiC-TaB2 composites

The oxidation resistance mechanism of SiC-B4C-xAl2O3 ceramics at 1400 °C in air atmosphere

Oxidation Resistance of In Situ Reaction/Hot Pressing Synthesized Ti2AlC–20% TiB2 Composite at 600–900 °C in Air

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Tribological behaviors of vacuum hot-pressed ceramic composites with enhanced cyclic oxidation and corrosion resistance

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

High temperature oxidation resistance of Y2O3 modified ZrB2-SiC coating for carbon/carbon composites

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

Effect of Si element on improving the oxidation resistance of hybrid (Ti5Si3 + TiC) particles reinforced Ti6Al4V matrix composites

Influences of the pre-oxidation time on the microstructure and flexural strength of monolithic B4C ceramic and TiB2-SiC/B4C composite ceramic