Abstract:TiB2‐TiN‐NiTi cermet materials are prepared by SPS. In this paper, the effect of different sintering process on the mechanical properties and microstructure of 74TiB2‐20TiN‐6NiTi are studied. And then the effect of holding time at different holding stages on the density, mechanical properties and microstructure are also investigated. It has the following conclusions: the TiB2‐TiN‐NiTi ceramic material was prepared by SPS method. The effects of different sintering processes on the mechanical properties and microstructure of 74TiB2‐20TiN‐6NiTi alloy were studied. Then the effects of holding time at different holding stages on the density, mechanical properties and microstructure of the alloy were studied. The conclusion is as follows: when the sintering temperature is 1650°C, the intermediate holding temperature is 900°C, the intermediate holding time is 3 min, and the final holding time is 5 min, the ceramic material with excellent comprehensive mechanical properties can be obtained. TiB2‐TiN‐NiTi cermet material was prepared by spark plasma sintering technology (SPS). The effects of the sintering process on their relative density, mechanical properties, and microstructure were studied with 74TiB2‐20TiN‐6NiTi as the composition system. The results showed that TiB2‐TiN‐based cermet material with the best mechanical properties was prepared under the sintering temperature of 1650°C and the holding time of 5 min. The relative density, flexural strength, fracture toughness, and hardness are 97.7%, 762.7 MPa, 5.5 MPa·m1/2, and 18.47 GPa, respectively. However, if the holding time keeps for 3 min under the sintering temperature of 900°C and then 5 min under the sintering temperature of 1650°C, the relative density, flexural strength, fracture toughness, and hardness of TiB2‐TiN‐based cermet reach 99.1%, 931.3 MPa, 5.8 MPa·m1/2, and 19.15 GPa, respectively. In comparison, they have been greatly improved by 1.4%, 22.1%, 5.5%, and 3.7%, respectively. The final holding time can also affect the mechanical properties of TiB2‐TiN‐based cermet material. When it is higher than 5 min, it will cause irregular growth and abnormal growth of grains, which can decrease the flexural strength of TiB2‐TiN‐based cermet material.

Densification and Mechanical Properties of Tic by Sps-Effects of Holding Time, Sintering Temperature and Pressure Condition

Investigation of TiC formation during ball-milling of elemental titanium and carbon

Effects of Y2O3 on the Densification and Fracture Toughness of SPS-sintered TiC

Preparation and Characterization of Tic-Sic Composites Sintered by Sps

Densification and microstructure evolution of W-TiC-Y2O3 during spark plasma sintering

Densification, Microstructure and Mechanical Performance of TiC/Fe Composites by Spark Plasma Sintering

Sintering and densification mechanisms of tantalum carbide ceramics

Effects of Process Parameters on Microstructure and Properties of TiC Reinforced Cu-Matrix Composites

Spark Plasma Sintering and Characterization of 2Y-TZP Ceramics

Investigation of the effect of pressure, sintering temperature and time on silicon carbide microstructure

Effect of temperature on the structure and mechanical properties of SiC–TiB2 composite ceramics by solid-phase spark plasma sintering

Effects of pore microstructures on thermal and mechanical properties of porous TiC fabricated by hot press sintering

Preparation of WC-Co Cemented Carbide by Spark Plasma Sintering: Microstructure Evolution, Mechanical Properties and Densification Mechanism

Effect of nano-TiC addition on sinterability and mechanical properties of TiC high temperature ceramics

Microstructure and mechanical properties of TiC steel-bonded carbides prepared by two-step sintering technique

Microstructure, Mechanical Properties, and Sintering Behavior of Ti3O-Fe2TiO4-TiC Composites

Numerical study on the warm compaction and solid-state sintering of TiC/316L composite powders from particulate scale

Fabrication of W–1 Wt.% TiC Composites by Spark Plasma Sintering

Rapid densification and mechanical properties of ultra-high-pressure sintered transition metal carbide ceramics

Effect of different sintering process on mechanical properties and microstructure of TiB2‐TiN‐based cermet material

Microstructures and mechanical properties of TiB2 composite ceramics with co-addition of Ti and TiC fabricated by SPS