Abstract:This study deals with the effect of conventional sintering and microwave sintering on the densification kinetics of Titanium Carbide (TiC) in the presence of Ni (1, 1.5, 2 wt%). TiC compacts were obtained after uniaxial pressing of powders synthesised by ball milling of Titanium and Carbon and sintering was done in the presence of Nickel. The samples prepared were subjected to conventional as well as microwave sintering. The XRD and SEM analysis were used for a study of the reaction of Ti and C powders upon addition of Ni, which reduced the sintering temperature to 1200 °C. The densification of TiC powders was due to the Ti-Ni eutectic system, the liquid phase formed at this temperature assisting the sintering process. The SEM images revealed the flake like structure of TiC in which the carbon diffused into Ti upon the addition of Ni, thereby supporting enhanced mass transfer. The XRD pattern showed the presence of Titanium Oxide (TiO2) along with TiC which resulted in non-uniform distribution of hardness. Maximum hardness was achieved in the conventional sintered compacts which gradually increased with increase in Ni addition. The presence of the oxide phase and the formation of micro cracks resulted in non-uniform hardness for microwave sintered compacts. The maximum hardness of conventional sintered compact (375 HLD) was nearly 1.5 times more than the maximum hardness of the microwave sintered compact (250 HLD). The density of the microwave sintered compact was found to be higher by 8% than with the conventionally sintered compact.

Microstructure and mechanical properties of TiC steel-bonded carbides prepared by two-step sintering technique

Investigation of TiC formation during ball-milling of elemental titanium and carbon

The Preparation Process, Microstructure and Properties of Cellular TiC-High Mn Steel-Bonded Carbide

Microstructure and mechanical properties of B4C–TiB2 ceramic composites prepared via a two-step method

Microstructure and mechanical properties of TiB2-40 wt% TiC composites: Effects of adding a low-temperature hold prior to sintering at high temperatures

Mechanical properties and microstructural evolution of pressureless sintered ceramics obtained from high-energy ball-milled TiB2–TiC powders

Microhomogeneous WC-TiC-Co composite powders with enhanced sinterability via a two-step carburization method

Effect of nano-TiC addition on sinterability and mechanical properties of TiC high temperature ceramics

Densification and Mechanical Properties of Tic by Sps-Effects of Holding Time, Sintering Temperature and Pressure Condition

Preparation and Characteristics of W–1 Wt.% TiC Alloy Via a Novel Chemical Method and Spark Plasma Sintering

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

Influence of TiC content on microstructure and mechanical properties of (Ta, Ti)C ceramics

Cr3C2 assisted ultrafast high-temperature sintering of TiC

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties

Study on Microstructures and Properties of Porous TiC Ceramics Fabricated by Powder Metallurgy

Improvement in Microstructure and Mechanical Properties of Ti(C, N) Cermet Prepared by Two-Step Spark Plasma Sintering

Microstructure Transformation and Mechanical Properties of TiC–TiB2 Ceramics Prepared by Combustion Synthesis in High Gravity Field

Effects of TiC formation on the microstructure and hardness of wear-resistant steel

Fabrication and properties of Ti3AlC2-based ceramics by two-step method

Preparation and Properties of Solidified TiC-TiB2 with Hypoeutectic, Eutectic and Hypereutectic Microstructures

EFFECTS OF TIC CONTENT ON SINTERED PROPERTIES OF TiCp/M2 HIGH SPEED STEEL COMPOSITES