Abstract:FePt:C thin films were deposited on CrRu underlayers by DC magnetron co-sputtering. The effects of C content, FePt:C film thickness and substrate temperature on the microstructural and magnetic properties of the epitaxial FePt (001) films were studied. Experimental results showed that even with 30 vol.% C doping, the FePt films could keep a (001) preferred orientation at 350 degrees C. When a FePt:C film was very thin (<5 nm), the film had a continuous microstructure instead of a granual structure with C diffused onto the film surface. With further increased film thickness, the film started to nucleate and formed a column microstructure over continuous FePt films. A strong exchange coupling in the FePt:C films was believed to be due to the presence of a thin continuous FePt layer attributed to the carbon diffusion during the initial stage of the FePt:C film growth. Despite the presence of a strong exchange coupling in the FePt:C (20 vol.% C) film, the SNR ratio of the FePt:C media was about 10 dB better than that of the pure FePt media. The epitaxial growth of the FePt:C films on the Pt layers was observed from high resolution TEM cross sectional images even for the films grown at about 200 degrees C. The TEM images did not show an obvious change in the morphology of the FePt:C films deposited at different temperatures (from 200 degrees C to 350 degrees C), though the ordering degree and coercivity of the films increased with increased substrate temperature. (C) 2008 Elsevier B.V. All rights reserved.

Effects of Cu Underlayer on the Growth and Magnetic Properties of Fept Thin Films on Mgo (001) Substrate

Influence of Cu underlayer on the high-frequency magnetic characteristics of as-sputtered FeCoSiN granular thin films

Effects of an Ultrathin Mgo Inserted Layer on the Magnetic Properties of Fept Films

Structural and Magnetic Properties of FePt Films Grown on Cr1-xMox Underlayers

Effects of Substrate on Structure and the Magnetic Properties of (001)-Textured FePt Films Grown at Low Temperature

Structural and magnetic properties of FePt films grown on Cr 1-x Mo x underlayers

Growth and Magnetism of Ultrathin Fe Films on Pt(100)

Coercivity, Microstructure and Magnetization Reversal Mechanism in Tini-Doped L1(0) Fept Thin Films

Improvement of magnetic property of L10‐FePt film by FePt∕Au multilayer structure

Development of ${\rm L}1_{0}$ FePt:C (001) Thin Films with High Coercivity and Small Grain Size for Ultra-High-Density Magnetic Recording Media

Modulation of Preferred Orientation and Easy Axis of Magnetic Anisotropy in L10 FePt Films with Cu Buffer Layers

Controlling the Crystallographic Orientation and Easy Axis of Magnetic Anisotropy in L 10 FePt Films with Cu Additive

Enhancement of L10 Ordered FePt by Pt Buffer Layer

Effect of Interfacial Diffusion on Microstructure and Magnetic Properties of Cu∕FePt Bilayer Thin Films

Magnetic and Magneto-Optical Properties of Perpendicularly C-Axis Orientated FePt Thin Films

Low-temperature Deposition of L10 FePt Films for Ultra-High Density Magnetic Recording

Microstructural and magnetic properties of L1 0 FePt C (0 0 1) textured nanocomposite films grown on different intermediate layers

Magnetic And Electric Properties Of Fe3o4 Thin Films Sputtered On Metallic Underlayer

Magnetic Anisotropy of L10-FePt Film on (001) LaAlO3

Effect of Carbon Additive on Microstructure Evolution and Magnetic Properties of Epitaxial FePt (001) Thin Films

Effects of SiO2 inserted layers on the Structure and magnetic properties of FePt (001) films