Effects of Thickness Ratio of Co to Pt Layer on Magnetic Properties and Microstructure of [Co/Pt]n Multilayer Films
Sea-Fue Wang,Yu-Ting Lin,Puneet Sharma,Yu-Shen Chen,Chuan-Fa Huang,A. Sun,Tsu-Ching Yang,Hsi-Chuan Lu,Yin-Cheng Ju
DOI: https://doi.org/10.1109/tmag.2015.2464321
IF: 1.848
IEEE Transactions on Magnetics
Abstract:[Co/Pt]<sub>n</sub> multilayer films were deposited on a glass substrate with a Pt underlayer by an alternative sputtering method. The effect of overall multilayer [CoPt]n thickness and the relative thickness of Co to Pt layers on the structural and magnetic properties were investigated. First, the thickness ratio of Co to Pt layers (Co:Pt = 4:3, 1:1, and 3:4) in [Co/Pt]n multilayer films was varied. Higher coercivity and out-of-plane squareness were found for the [Co<sub>1 nm</sub>/Pt<sub>0.75 nm</sub>]<sub>n</sub> and [Co<sub>1 nm</sub>/P<sub>t1 nm</sub>]<sub>n</sub> multilayer films. The total thickness of multilayers was varied from 3.5 to 8 nm. When the Co to Pt layers thickness ratio was changed to 3:4, the magnetic performance was declined. Furthermore, the thickness ratio of Co to Pt layers was kept constant to 1:1, and the Co and Pt layer thickness in [C<sub>ox nm</sub>/P<sub>tx nm</sub>]<sub>n</sub> film was varied. The highest coercivity of 2.1 kOe was obtained in the [Co<sub>0.5</sub>/Pt<sub>0.5</sub>]<sub>4</sub> film. The magnetic properties were decreased with further increase in the Co and Pt layer thickness. In this paper, we demonstrated that [Co/Pt]n multilayer films with the suitable thickness ratio of Co to Pt layers are beneficial to prepare CoPt thin films with perpendicular magnetic anisotropy.
Materials Science,Physics