Modulation of Preferred Orientation and Easy Axis of Magnetic Anisotropy in L10 FePt Films with Cu Buffer Layers

YF Ding,JS Chen,E Liu

DOI: https://doi.org/10.1016/j.surfcoat.2004.10.077

IF: 4.865

2005-01-01

Surface and Coatings Technology

Abstract:The crystallographic orientation and easy axis of magnetic anisotropy in L10 FePt films were successfully modulated with Cu buffer layers. The FePt film directly grown on the Cr90Mo10 underlayer showed a (001) preferred orientation with out-of-plane magnetic anisotropy. As the Cu buffer layer thickness was ≥4 nm, the FePt films showed a (110) preferred orientation with in-plane magnetic anisotropy. The FePt films on the Cr90Mo10 underlayers showed a continuous microstructure, while they showed a particle-like structure when the Cu buffer layers were used. The grain size of the FePt films increased with increasing Cu buffer layer thickness. The cross-sectional image revealed that the FePt film with 12 nm Cu buffer layer had columnar structure. The experimental results suggested that the Cu films can be a promising buffer layer for controlling the texture and easy axis of the magnetic anisotropy of FePt films.