Structural and magnetic properties of FePt films grown on Cr 1-x Mo x underlayers

Y.F. Ding,J.S. Chen,E. Liu

DOI: https://doi.org/10.1007/s00339-005-3262-9

2005-01-01

Applied Physics A

Abstract:FePt films were deposited on Cr 1-x Mo x underlayers by dc magnetron sputtering. The effects of the Mo content in the underlayers, underlayer thickness, substrate temperature, and FePt film thickness on the structural and magnetic properties of the FePt films were studied. Experimental results showed that the (200) textured Cr 90 Mo 10 film was a promising underlayer for promoting the growth of the L1 0 FePt films with (001) preferred orientation at relatively low temperatures. With the Cr 90 Mo 10 underlayers, the ordering process of the FePt films could start at 200 °C. Both the ordering degree and the out-of-plane coercivity (H c ) of the FePt films increased with an increase in substrate temperature. When the substrate temperature was ≥250 °C, the FePt films grown on the Cr 90 Mo 10 underlayers could have the (001) preferred orientation. The FePt films grown on the Cr 90 Mo 10 underlayers at different temperatures showed a continuous microstructure. The out-of-plane coercivities H c decreased while the ordering degree increased with increased FePt film thickness, which could be due to the variation of the magnetic reversal mechanism from rotation predominant mode to domain wall motion predominant mode.