Abstract:MgB2 superconductors with unique microstructures were rapidly fabricated at low temperatures, and exhibited significantly improved critical current density (J(c)). According to the microstructure observations, the prepared samples consisted of lamellar nano MgB2 grains with many embedded nanoimpurities (about 10 nm). The formation of these lamellar nano MgB2 grains is associated with the presence of a local Mg-Cu liquid at sintering temperatures as low as 575 degrees C. The ball milling treatment of the original powders also plays a positive role in the growth of lamellar grains. Based on an analysis of the relationship between resistivity and temperature, the lamellar nano MgB2 grains in the prepared sample possess better grain connectivity than the typical morphology of MgB2 samples prepared by traditional high-temperature sintering. Furthermore, the presence of many nano MgB2 grain boundaries and nano impurities in the prepared sample can obviously increase the flux pinning centers in accordance with the analysis of flux pinning behavior. Both factors mentioned above contribute to the significant improvement in J(c) from low field to relative high field. The method developed in the present work is an effective and low-cost way to further enhance J(c) in MgB2 superconductors across a wide range of applied magnetic fields without using expensive nanometer-sized dopants.

The Synthesis of Lamellar Nano MgB2 Grains with Nanoimpurities, Flux Pinning Centers and Their Significantly Improved Critical Current Density

Significant Improvement in the Critical Current Density of Mgb2 Bulks in Situ Sintered at Low Temperature by Excess Mg Addition

The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks

Significant Enhancement of Flux Pinning in Mgb2 Superconductor Through Nano-Si Addition

Excellent Jc in the low-temperature sintered MgB2 superconductors consisted of uncompleted MgB2 phase and residual Mg

Amorphous B coated Mg nanopowder induces low angle grain boundaries and enhances J c of MgB 2 wire

Significant Improvement of Jc in MgB2 Bulk Superconductor Using Ball-Milled High-Purity Crystalline Boron

Confinement of Self-Generated Mg(BH4)2 Particles for Simultaneously Enhanced Flux Pinning and Grain Connectivity in Polycrystalline H-doped MgB2

Effect of Nano-SiC and Nano-Si Doping on Critical Current Density of MgB 2

The effect of ball-milling treatment of original powders on the sintering process and critical current density of graphite-doped MgB 2 bulks

High Critical Current Density of a MgB 2 Bulk Superconductor High-pressure Synthesized Directly from the Elements

Improved flux pinning behaviour in bulk MgB<sub>2</sub> achieved by nano-SiO<sub>2</sub> addition

Research Progress of MgB2 Superconducting Materials Prepared by High-energy Ball Milling

Improvement of Critical Current Density in MgB2 Superconductors by Zr Doping at Ambient Pressure

Phase Formation and Superconductive Properties of Cu Doped MgB2 Sintered with Milled B Powder

Variation of MgB2 growth mode and enhancement of critical current density by instantaneously 800 °C-triggered low-temperature sintering

Enhanced Flux Pinning In Zr-Doped Mgb2 Bulk Superconductors Prepared At Ambient Pressure

Superconducting properties and growth mechanism of layered structure in MgB 2 bulks with Cu/Y 2 O 3 co-doping

Microstructure and Superconducting Properties of MgB2 Bulks Prepared from Mg + B + Mg(BH4)2 Composites

Improved Superconducting Properties in Bulk MgB2prepared by High-Energy Milling of Mg and B Powders

Low-temperature synthesis of superconducting nanocrystalline MgB2