Abstract:Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macrostructure and grain size. Grain size increased with HT time at both 600C and 700C. Jc and hence Fp decreased monotonically but not linearly with grain size. Overall, it was observed that at 700C, the MgB2 reaction was more or less complete after as little as 30 min; at 600C, full reaction completion did not occur until 71 h. into the HT. Transport, Jct(B) was measured in a perpendicular applied field, and the magnetic critical current densities, Jcm\bot(B) and Jcm{\phi}(B), were measured in perpendicular and parallel (axial) applied fields, respectively. Particularly noticeable was the premature dropoff of Jcm\bot(B) at fields well below the irreversibility field of Jct(B). This effect is attributed to the fibrous macrostructure and its accompanying anisotropic connectivity. Magnetic measurements with the field directed along the strand axis yielded a critical density, Jcm\bot(B), for current flowing transversely to the strand axis that was less than and dropped off more rapidly than Jct(B). In the conventional magnetic measurement, the loop currents that support the magnetization are restricted by the lower of Jct(B) and Jcm{\phi} (B). In the present case the latter, leading to the premature dropoff of the measured Jcm(B) compared to Jct(B) with increasing field. This result is supported by Kramer plots of the Jcm{\phi} (B) and Jct(B) data which lead to an irreversibility field for transverse current that is very much less than the usual transport-measured longitudinal one, Birr,t.

Microstructure and high critical current of powder in tube MgB2

High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes

Influence of the Preparation Process on Microstructure, Critical Current Density and Tc of MgB2 Powder-In-Tube Wires

Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires

Fabrication and Properties of Multifilamentary MgB2 Wires by In-Situ Powder-in-tube Process

Fabrication and Superconducting Properties of MgB2 Wires with Amorphous Carbon Doping by In-situ Powder-in-tube Method

Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in-situ processed MgB2 strands

Transport and magnetic Jc of MgB2 strands and small helical coils

High transport critical currents in dense, metal-clad superconductor wires of MgB2

Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex-situ tapes

High-energy ball milling and synthesi temperature study to improve superconducting properties of MgB2 ex-situ tapes and wires

The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks

Supercurrents in magnesium diboride/metal composite wire

Investigation of Layered Structure Formation in MgB2 Wires Produced by the Internal Mg Coating Process under Low and High Isostatic Pressures

The Effect of Zrsi2 and Sic Doping on the Microstructure and J(C)-B Properties of Pit Processed Mgb2 Tapes

Amorphous B coated Mg nanopowder induces low angle grain boundaries and enhances J c of MgB 2 wire

Large transport critical currents in unsintered MgB2 superconducting tapes

Superconducting properties of the powder-in-tube Cu-Mg-B and Ag-Mg-B wires

Improved superconducting properties of MgB2

Effect of Heat Treatments under High Isostatic Pressure on the Transport Critical Current Density at 4.2 K and 20 K in Doped and Undoped MgB2 Wires

Improved Superconducting Properties in Bulk MgB2 Prepared by High Energy Milling of Mg and B Powder