Superconducting properties of the powder-in-tube Cu-Mg-B and Ag-Mg-B wires

B. A. Glowacki,M. Majoros,M. E. Vickers,B. Zeimetz
DOI: https://doi.org/10.1016/S0921-4534%2802%2900986-3
2001-09-05
Abstract:The new class of Mg-B superconducting conductors was prepared using the standard in-situ powder-in-tube, PIT, method where Mg+2B mixture was used to fill the copper and silver tubes. Study of the intergranular current, grain connectivity and superconducting phases in wires were conducted by AC susceptibility measurements and direct four point transport measurements. Using SQUID magnetometer, magnetisation versus magnetic field (M-H) curves of the round wires after reactive diffusion were measured at temperatures 5K and magnetic field up to 5T to define the Jcmag . The direct current density measurements of the in-situ Cu-MgB2 performed at 4.2K gave the value of 10^9 Am-2 .
Superconductivity,Materials Science
What problem does this paper attempt to address?
This paper aims to explore the superconducting properties of Cu - Mg - B and Ag - Mg - B superconducting wires prepared by the Powder - in - Tube (PIT) method. Specifically, the researchers focused on the inter - granular currents, grain connectivity, and characteristics of the superconducting phase of these wires. In the study, AC susceptibility measurement and direct four - point transmission measurement methods were used to evaluate the properties of these superconducting wires. And the relationship curve between magnetization and magnetic field (\(M - H\) curve) of circular wires was measured by SQUID magnetometer at a temperature of 5K and a magnetic field strength up to 5 Tesla to define the critical magnetization current density (\(J_{c\text{mag}}\)). In addition, the paper also paid special attention to the performance changes of these superconducting wires under different heat - treatment conditions, including the influence of the sintering process in different temperatures and atmospheres on the material properties. The study found that different sintering conditions would lead to changes in the critical transition temperature (\(T_c\)), critical current density (\(J_c\)), and magnetization properties of the material. Some samples showed an abnormal decrease in susceptibility around about 50K, which might be caused by factors such as the multi - phase structure inside the material or element diffusion. In summary, the problem that this paper attempts to solve is how to improve the mechanical strength, critical current density, and overall performance of Cu - Mg - B and Ag - Mg - B superconducting wires by optimizing the preparation process and heat - treatment conditions, thereby promoting the practical utilization of these new superconducting materials in commercial applications.