Abstract:We prepared a series of MgB2 bulk samples under different temperatures, holding time and increasing rates in temperature by the solid state reaction. The thermodynamic behavior and phase formation in the Mg-B system were studied by using DTA,XRD and SEM. The results indicate that the formation of the MgB2 phase is very fast and the high increasing rate in temperature is necessary to obtain high quality MgB2. In addition, the effects of the Zr-doping in Mg1-xZrxB2 bulk samples fabricated by the solid state reaction at ambient pressure on phase compositions, microstructure and flux pinning behavior were investigated by using XRD, SQUID magnetometer, SEM and TEM. Critical current density Jc can be significantly enhanced by the Zr-doping and the best data are achieved in Mg0.9Zr0.1B2. For this sample, Jc values are remarkably improved to 1.83×106 A/cm2 in self-field and 5.51×105 A/cm2 in 1 T at 20 K. Also, high quality MgB2/Ta/Cu wires and tapes with and without Ti-doping, MgB2/Fe wires and 18 filament MgB2/NbZr/Cu tapes were fabricated by the powder-in-tube (PIT) method at ambient pressure. The phase compositions, microstructure features and flux pinning properties were studied. The results suggest that Fe is thebest metal for these sheaths. MgB2/Fe wires exhibit very high Jc at high temperatures and high fields. Jc values reach as high as 1.43×105 A/cm2 (4.2 K, 4 T) and 3.72×104 A/cm2 (15 K, 4 T).

The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks

Improved Superconducting Properties in Bulk MgB2prepared by High-Energy Milling of Mg and B Powders

Improved Superconducting Properties in Bulk MgB2 Prepared by High Energy Milling of Mg and B Powder

The Synthesis of Lamellar Nano MgB2 Grains with Nanoimpurities, Flux Pinning Centers and Their Significantly Improved Critical Current Density

The Influence of Cooling Velocity on the Microstructure and Superconducting Properties of MgB_2 Bulks Prepared by High Energy Milling

The effect of ball-milling treatment of original powders on the sintering process and critical current density of graphite-doped MgB 2 bulks

Significant Improvement in the Critical Current Density of Mgb2 Bulks in Situ Sintered at Low Temperature by Excess Mg Addition

Significant Improvement of Jc in MgB2 Bulk Superconductor Using Ball-Milled High-Purity Crystalline Boron

High-energy ball milling and synthesi temperature study to improve superconducting properties of MgB2 ex-situ tapes and wires

Superconducting Properties and Microstructure in MgB 2 Bulks, Wires and Tapes

Research Progress of MgB2 Superconducting Materials Prepared by High-energy Ball Milling

Nanoparticles of the Superconductor MgB2: Structural Characterization and in Situ Study of Synthesis Kinetics

Effects of Ball Milling on the Sintering Process and Superconducting Properties of $(\hbox{mgb}_{2})_{0.96}\hbox{ni}_{0.04}$ Bulks

Effect of amorphous carbon doping on microstructure and superconducting properties of MgB2 bulk

Influences of Heat Treatment and Doping on Microstructure and Superconducting Properties of MgB2 Superconductor

Microstructure and Superconducting Properties of MgB2 Bulks Prepared from Mg + B + Mg(BH4)2 Composites

Exploratory Study of the Synthesis of Nanocrystalline MgB2 Superconducting Compound by Controlled and Electrical Discharge Assisted Mechanical Alloying

Phase Formation and Superconductive Properties of Cu Doped MgB2 Sintered with Milled B Powder

Superconducting properties of nanocrystalline MgB$_2$

Synergism Effect of Pb Doping and Microstructure Optimization on the Superconducting Properties of Bi-2212 Ceramics

Strong influence of precursor powder on the critical current density of Fe-sheathed MgB2 tapes