Improved flux pinning behaviour in bulk MgB₂ achieved by nano-SiO₂ addition

X F Rui,Y Zhao,Y Y Xu,L Zhang,X F Sun,Y Z Wang,H Zhang

DOI: https://doi.org/10.1088/0953-2048/17/4/022

2004-01-01

Abstract:Bulk MgB2 with SiO2 nanoparticles added has been synthesized using a simple solid-state reaction route. The lattice constant in the c direction increases with additive content due to a small amount of Si being doped into the lattice of the MgB2; however, T-c is almost fixed at 37.2 K. The addition Of SiO2 nanoparticles also improves the J(c)-H and H-irr-T characteristics of MgB2 when the additive content is lower than 7%. At 20 K and 1 T, J(c) for the sample with 7% additive content reaches 2.5 x 10(5) A cm(-2). Microstructural analysis reveals that a high density Of MgSi2 nanoparticles (10-50 nm) exists inside the MgB2 grains, leading to the formation of a nanocomposite superconductor.