The doping effect of multiwall carbon nanotube on MgB2/Fe superconductor wire

J. H. Kim,W. K. Yeoh,M. J. Qin,X. Xu,S. X. Dou

DOI: https://doi.org/10.1063/1.2209188

2006-03-22

Abstract:We evaluated the doping effect of two types of multiwall carbon nanotube (CNT) with different aspect ratios on MgB2/Fe monofilament wires. Relationships between microstructure, magnetic critical current density (Jc), critical temperature (Tc), upper critical field (Hc2), and irreversibility field (Hirr) for pure and CNT doped wires were systematically studied for sintering temperature from 650oC to 1000oC. As the sintering temperature increased, Tc for short CNT doped sample slightly decreased, while Tc for long CNT doped sample increased. This indicates better reactivity between MgB2 and short CNT due to its small aspect ratio and substitution of carbon (C) from short CNT for boron (B) occurs. In addition, short CNT doped samples sintered at the high temperatures of 900oC and 1000oC exhibited excellent Jc, and that value was approximately 104 A/cm2 in fields up to 8 T at 5 K. This suggests that short CNT is a promising carbon source for MgB2 superconductor with excellent Jc. In particular, inclusion of nanosized MgO particles and substitution of C into the MgB2 lattice could result in strong flux pinning centers.

Superconductivity

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to evaluate the doping effect of multi - wall carbon nanotubes (CNT) on MgB₂/Fe superconducting wires, especially the influence of CNTs with different aspect ratios on the microstructure, magnetic critical current density \(J_c\), critical temperature \(T_c\), upper critical magnetic field \(H_{c2}\) and irreversible field \(H_{\text{irr}}\) of MgB₂/Fe single - filament wires. Specifically, the researchers systematically studied the influence of doping short CNTs and long CNTs on the properties of MgB₂/Fe wires at different sintering temperatures from 650°C to 1000°C, in order to find the optimal doping scheme for optimizing the performance of MgB₂ superconductors.

### Main research questions:
1. **Evaluation of doping effect**: The influence of CNTs with different aspect ratios (short CNTs and long CNTs) on the microstructure, magnetic critical current density \(J_c\), critical temperature \(T_c\), upper critical magnetic field \(H_{c2}\) and irreversible field \(H_{\text{irr}}\) of MgB₂/Fe superconducting wires.
2. **Influence of sintering temperature**: The specific changes in the properties of MgB₂/Fe wires due to CNT doping at different sintering temperatures (from 650°C to 1000°C).
3. **Discussion of reaction mechanism**: The reaction mechanism between short CNTs and long CNTs and MgB₂ and its influence on superconducting properties, especially under high - temperature sintering conditions.

### Key findings:
- **Critical temperature \(T_c\)**: As the sintering temperature increases, the \(T_c\) of the short - CNT - doped samples decreases slightly, while the \(T_c\) of the long - CNT - doped samples increases. This indicates that short CNTs have better reactivity with MgB₂, and the phenomenon of carbon (C) replacing boron (B) from short CNTs is more significant.
- **Magnetic critical current density \(J_c\)**: The short - CNT - doped samples exhibit excellent \(J_c\) when sintered at 900°C and 1000°C, reaching approximately \(10^4 \, \text{A/cm}^2\) at an 8T magnetic field. This indicates that short CNTs are an effective carbon source for increasing the \(J_c\) of MgB₂ superconductors.
- **Upper critical magnetic field \(H_{c2}\) and irreversible field \(H_{\text{irr}}\)**: Both \(H_{c2}\) and \(H_{\text{irr}}\) of the short - CNT - doped samples are higher than those of the long - CNT - doped samples, indicating that short CNTs enhance the pass - band scattering of the superconductor, shortening the mean free path and coherence length.

Through these studies, the authors aim to provide theoretical basis and technical support for the performance optimization of MgB₂ superconducting materials.