Effect of SiC-Impurity Layer and Growth Temperature on MgB2 Superconducting Tapes Fabricated by HPCVD
Mahipal Ranot,Won Kyung Seong,Soon‐Gil Jung,Won Nam Kang,Jinho Joo,Chan‐Joong Kim,Byung‐Hyuk Jun,Sangjun Oh,Soon-Gil Jung,Chan-Joong Kim,Byung-Hyuk Jun
DOI: https://doi.org/10.1002/cvde.201106935
2012-03-01
Chemical Vapor Deposition
Abstract:Abstract The influence of SiC‐impurity layer and growth temperature on microstructure and superconducting properties are studied for MgB 2 superconducting tapes. A pulsed laser deposition (PLD) system is used for the deposition of amorphous SiC‐impurity layers on flexible metallic Cu(001) tapes. The MgB 2 superconducting tapes are fabricated by growing MgB 2 films on the top of SiC/Cu tapes, over a wide temperature range of 460–600 °C, by using hybrid physical (HP) CVD system. Among all tapes, the MgB 2 /SiC/Cu tape deposited at a temperature of 540 °C has the highest T c of ∼37.7 K. Scanning electron microscopy (SEM) images reveal hexagonal‐shaped MgB 2 grains with good connectivity, and their sizes are found to vary with growth temperature. When compared to MgB 2 /Cu tapes, the MgB 2 /SiC/Cu tapes exhibit an opposite trend in the dependence of critical current density ( J c ) with deposition temperatures. The improved J c ( H ) behavior can be explained on the basis of the enhanced flux pinning force density ( F p ) for MgB 2 /SiC/Cu tapes upon increasing the growth temperature We report on the effect of SiC‐impurity layer as well as growth temperature on the superconducting properties of MgB 2 tapes. Firstly, SiC‐impurity layers were grown on Cu (001) tapes by pulsed laser deposition system. Subsequently, MgB 2 films were fabricated on SiC/Cu tapes over a wide temperature range of 460–600 °C by using hybrid physical‐chemical vapor deposition system. All the prepared tapes were characterized by XRD, SEM, resistivity and magnetization measurements. The MgB 2 /SiC/Cu tapes showed improved flux pinning and enhanced critical current density ( J c ) than the MgB 2 /Cu tapes. Our results demonstrate that HPCVD is a promising technique to fabricate thick MgB 2 superconducting tapes with high J c values for large scale applications.
English Else