Microstructures and mechanical properties of additively manufactured alumina ceramics with digital light processing
Mingze Xin,Zhanqiang Liu,Bing Wang,Qinghua Song
DOI: https://doi.org/10.1007/s43452-022-00588-1
IF: 4.042
2022-12-30
Archives of Civil and Mechanical Engineering
Abstract:Digital light processing (DLP) technology has presented great potential to fabricate ceramic structures including alumina component, yet the mechanical properties of DLP-manufactured ceramics are still difficult to be guaranteed. The enhancement of mechanical properties of DLP-fabricated ceramic materials is challenging and imperative in the field of industrial application. This paper investigates the printing and heat treatment processes of additively manufactured ceramic to achieve defect-free Al 2 O 3 ceramic with high performance. Firstly, Al 2 O 3 ceramic slurry with a high solid content of 55 vol.% and viscosity of 6.04 Pa·s (at the shear rate of 100 s −1 ) is prepared. Then, Al 2 O 3 ceramic is manufactured with digital light processing, debinding and sintering processes sequentially. Thirdly, the effects of sintering temperatures on the shrinkage, density, microstructure, and mechanical properties of the Al 2 O 3 ceramics are analyzed. The shrinkage, density, and flexural strength of the sintered ceramic increase with temperature; the microhardness shows a non-monotonic trend with the increase of sintering temperature. Finally, the influence mechanism of sintering temperature on microstructures and mechanical properties of the DLP-fabricated ceramics is interpreted and discussed. The ceramic grains grow and combine to form long columnar grains during higher sintering temperatures. The density, microhardness and flexural strength of the Al 2 O 3 ceramics sintered at 1600 °C are achieved 3.51 g/cm 3 , 17.71 GPa and 175.8 MPa, respectively.
engineering, mechanical,materials science, multidisciplinary, civil