Preparation of Translucent PolycrystaUine Alumina Ceramics Via Liquid Precursor Infiltration Technique Introducing Additives

王峰,谢志鹏,孙加林,千粉玲,廖艳梅,刘冠伟

DOI: https://doi.org/10.14062/j.issn.0454-5648.2012.06.015

2012-01-01

Abstract:Additives of MgO, Y203, La2Os for fabrication of translucent polycrystaUine alumina (TPCA) ceramics were introduced by infiltration technique into pre-sintered alumina green bodies in the form of Mg(NO3)2, Y(NO3)3, La(NO3)3 aqueous precursor solutions and sintered in H2 atmosphere at temperature of 1 830 ℃ for 2 h. Microstructure and real in-line transmission of TPCA ceramics were characterized by scanning electron microscope and UV-visible spectrophotometer. The results indicated that the homogeneity of the introduced additives was enhanced through infiltration technology, compared with the conventional ball-milling method. With high micro-structural homogeneity and grain size in 20-50 μm, samples prepared by infiltration reached the highest real in-line transmission of 38.7% (λ = 800 nm, sample thickness of 0.8 mm) from wavelength of 300 to 800 nm. However, the highest real in-line transmission of TPCA ceramics prepared by conventional ball-milling method was only 12.3% (2 = 800 nm, sample thickness of 0.8 mm) due to the inhomogeneous microstructure and obvious residual pores. The real in-line transmission of TPCA ceramics can be greatly improved through introducing additives by infiltration technique.