Abstract:In this paper, Mg-9.5Gd-4Y–2Zn-0.5Zr cylindrical parts were prepared by the conventional backward extrusion (CBE) process and rotating backward extrusion (RBE) process. The effects of the two processes on the microstructure and mechanical properties of different orientation regions of rare earth magnesium alloy were analyzed and compared. The RBE process introduces a torsional shear quantity based on the CBE process. By changing the direction of plastic flow, has a positive effect on the elongation (EL) of the alloy. It was found that dynamic recrystallization (DRX) occurred in both CBE and RBE processes. With the transition of deformation, the strain continues to accumulate, and the DRX mechanism changes from discontinuous dynamic recrystallization (DDRX) to continuous dynamic recrystallization (CDRX). Compared with the CBE process, the grain refinement of the RBE process is more significant. After deformation, a more significant heterostructure is obtained in the RBE-45° region, and the average grain size reaches 24.7 μm. The ultimate tensile strength (UTS), yield strength (YS), and EL of the alloy in this region are 292.5 ± 7.7 MPa, 226.6 ± 7.4 MPa, and 21.5 ± 1.3 %, respectively. Although the strength is slightly lower than that of CBE alloy, better plasticity is obtained. The excellent strength-toughness synergy is attributed to the synergistic effect between heterogeneous regions of non-uniform microstructure. This study provides some theoretical guidance for the industrial production of large-size magnesium alloy cylindrical parts and subsequent applications.

Effect of backward extrusion on microstructure and mechanical properties of Mg-Gd based alloy

Numerical and Experimental Investigation on Hot Backward Extrusion Process of Mg-Gd-Y-Zn-Zr Magnesium Alloy

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Effects of backward extrusion on mechanical and degradation properties of Mg-Zn biomaterial.

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Microstructure and Mechanical Properties of Moderate-Speed Extrudable Mg-Gd-Sm-Zr Alloy

Effect of Extrusion Parameters on Microstructure and Mechanical Properties of Mg-7.5Gd-2.5Y-3.5Zn-0.9Ca-0.4Zr (wt%) Alloy

Mechanism of high-strength and ductility of Mg-RE alloy fabricated by low-temperature extrusion and aging treatment

Effect of Sm on microstructures and mechanical properties of Mg-Gd(-Sm)-Zr alloys by hot extrusion and aging treatment

Mechanical properties of Mg-Gd-Zr alloy by Nd addition combined with hot extrusion

Microstructure Evolution and Dynamic Precipitation Behavior of Mg–10Gd–4Y–1Sm–0.5Zr Alloy During Backward Hot Extrusion

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Effects of pre-aging on microstructure evolution and deformation mechanisms of hot extruded Mg–6Zn–1Gd–1Er Mg alloys

Effects of grain refinement and precipitate strengthening on mechanical properties of double-extruded Mg-12Gd-2Er-0.4Zr alloy

Effect of extrusion process on the mechanical and in vitro degradation performance of a biomedical Mg-Zn-Y-Nd alloy

Improved mechanical performance of double-pass extruded Mg-Gd-Er-Zr alloys with various rare earth contents

High elongation heterostructure rare earth magnesium alloy based on rotating backward extrusion process

The Development of a High-Strength Mg-10.3Gd-4.4Y-0.9Zn-0.7Mn Alloy Subjected to Large Differential-Thermal Extrusion and Isothermal Aging

Effect of Thermo-Mechanical Treatment on the Microstructure and Mechanical Properties of a Mg–6Gd–2Nd–0.5Zr Alloy

Study on the Mutual Effect of La and Gd on Microstructure and Mechanical Properties of Mg-Al-Zn Extruded Alloy

Effect of extrusion temperature on microstructure and mechanical properties of Mg-8.5Gd-2.3Y-l.8Ag- 0.4Zr alloy solid state recycled by hot extrusion