Abstract:In this study, ultrafine HfB 2 powders with low oxygen were synthesized by a flocculating settling process which yielded ceramic precursors and subsequent carbo/borothermal reduction of the precursors. The liquid phase precursor method can achieve uniform mixing of components at the molecular level through multiple complexation reactions, and then realize the carbo/borothermal reduction reaction at a lower temperature to obtain ultrapure HfB 2 powders. The as-resulted quasi-spherical HfB 2 powders under the optimum conditions (atomic molar ratio M:B:C = 1:2.8:10) calcined at 1500 & DEG;C for 1 h have an average particle size of 205 nm and an oxygen content of 0.097 wt.%. Detailed analysis of the phase evolution of precursors shows that the formation of HfB 2 particles is a mass diffusion mode from the external to internal HfO 2 cores. We reveal that below 1300 & DEG;C, HfC is not an intermediate product of HfB 2 powder during the transition of precursors. Instead, HfC was formed as a by-product at high temperatures in the carbo/borothermal reduction process. The proposed formation mechanism of HfB 2 is completely different from the traditional two-step transformation method. After the sintering of the ultrafine powders, the HfB 2 ceramics show a relative density of 96.1% and superior mechanical properties compared to other works. Furthermore, by simply replacing the initial metal source, chlorinated group IV and V transitional metals (Ti, Zr, Ta, Nb) can also convert into high-purity and ultrafine diborides. This work shows that flocculating settling assisted carbo/borothermal reduction has potential in lot size production of various high-purity and ultrafine boride powders.& COPY; 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Synthesis of Submicrometer HfB2 Powder and Its Densification

Synthesis and Formation Mechanism of HfB2 Ultrafine Powders with Low Oxygen Via Flocculating Settling Assisted Process and Carbo/borothermal Reduction

Pressureless densification of HfB2-based ceramics using HfB2 powders by borothermal reduction

Synthesis of superfine high-entropy metal diboride powders

Synthesis of High‐purity High‐entropy Metal Diboride Powders by Boro/carbothermal Reduction

Synthesis of Ultra-Fine and High-Pure Zirconium Diboride Powders Using Solution-Based Processing

A Facile Route for the Synthesis of High‐entropy Transition Carbides/borides at Low Temperatures

Low Temperature-Rapid Preparation of HfB2–SiC Powders by Microwave/molten Salt Assisted Boro/carbothermal Reduction

Low temperature synthesis of high‐entropy (Hf0.2Ti0.2Mo0.2Ta0.2Nb0.2)B2 powders combined with theoretical forecast of its elastic and thermal properties

Low-temperature densification of high entropy diboride based composites with fine grains and excellent mechanical properties

Powder synthesis, densification, microstructure and mechanical properties of Hf-based ternary boride ceramics

Molten Salt Synthesis, Formation Mechanism, and Oxidation Behavior of Nanocrystalline HfB 2 Powders

(Hf0.99Ta0.01)B2-based ceramics prepared by pressureless sintering with boron additive

Dense and pure high-entropy metal diboride ceramics sintered from self-synthesized powders via boro/carbothermal reduction approach

Fabrication of High‐purity HfSi2 Powder Via Molten Salt‐assisted Magnesium Thermal Reduction

Low-temperature synthesis of nanosized metal borides through reaction of lithium borohydride with metal hydroxides or oxides

Synthesis and Characterization of High-Purity, High-Entropy Diboride Ceramic Powders by a Liquid Phase Method

Strengthening Hf0.95Ta0.05B2 Ceramic With Ultrafine Grains and High-density Dislocations

Synthesis of High‐entropy Diboride Nanopowders Via Molten Salt‐mediated Magnesiothermic Reduction

Carbothermal Reduction Synthesis Of Zirconium Diboride Powders Assisted By Microwave

Dense HfB2 ceramics fabricated by high-energy ball milling and spark plasma sintering