Abstract:In this study, ultrafine HfB 2 powders with low oxygen were synthesized by a flocculating settling process which yielded ceramic precursors and subsequent carbo/borothermal reduction of the precursors. The liquid phase precursor method can achieve uniform mixing of components at the molecular level through multiple complexation reactions, and then realize the carbo/borothermal reduction reaction at a lower temperature to obtain ultrapure HfB 2 powders. The as-resulted quasi-spherical HfB 2 powders under the optimum conditions (atomic molar ratio M:B:C = 1:2.8:10) calcined at 1500 & DEG;C for 1 h have an average particle size of 205 nm and an oxygen content of 0.097 wt.%. Detailed analysis of the phase evolution of precursors shows that the formation of HfB 2 particles is a mass diffusion mode from the external to internal HfO 2 cores. We reveal that below 1300 & DEG;C, HfC is not an intermediate product of HfB 2 powder during the transition of precursors. Instead, HfC was formed as a by-product at high temperatures in the carbo/borothermal reduction process. The proposed formation mechanism of HfB 2 is completely different from the traditional two-step transformation method. After the sintering of the ultrafine powders, the HfB 2 ceramics show a relative density of 96.1% and superior mechanical properties compared to other works. Furthermore, by simply replacing the initial metal source, chlorinated group IV and V transitional metals (Ti, Zr, Ta, Nb) can also convert into high-purity and ultrafine diborides. This work shows that flocculating settling assisted carbo/borothermal reduction has potential in lot size production of various high-purity and ultrafine boride powders.& COPY; 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Dense HfB2 ceramics fabricated by high-energy ball milling and spark plasma sintering

Densification, microstructure and properties of ultra-high temperature HfB2 ceramics by the spark plasma sintering without any additives

Dense and pure high-entropy metal diboride ceramics sintered from self-synthesized powders via boro/carbothermal reduction approach

Low-temperature densification of high entropy diboride based composites with fine grains and excellent mechanical properties

Low temperature sintering of Hf0.95Nb0.05B2-based ceramics with submicron-scaled grains and enhanced mechanical properties

Pressureless densification of HfB2-based ceramics using HfB2 powders by borothermal reduction

Ultra-fast high-temperature synthesis and densification of high-entropy diborides and diboride-carbide ceramics

Fabrication of ultra-fine grained Hf-based materials with superior hardness and temperature-independent electrical conductivity by a combination of high-energy ball milling and spark plasma sintering

Synthesis and Formation Mechanism of HfB2 Ultrafine Powders with Low Oxygen Via Flocculating Settling Assisted Process and Carbo/borothermal Reduction

High‐pressure sintering of ultrafine‐grained high‐entropy diboride ceramics

Effect of mechanical milling on microstructure evolution and mechanical properties of Al–Zn–Mg–Cu–Si alloy fabricated via spark plasma sintering

Optimal preparation of high-entropy boride-silicon carbide ceramics

First-principles prediction, fabrication and characterization of (Hf0.2Nb0.2Ta0.2Ti0.2Zr0.2)B2 high-entropy borides

(Hf0.99Ta0.01)B2-based ceramics prepared by pressureless sintering with boron additive

Powder synthesis, densification, microstructure and mechanical properties of Hf-based ternary boride ceramics

Low-temperature Rapid Synthesis of Ultrafine Hafnium Carbide Ceramic Powders

The Effect of B4C on the Microstructure and Thermo-Mechanical Properties of HfB2-based Ceramics

Strengthening Hf0.95Ta0.05B2 Ceramic With Ultrafine Grains and High-density Dislocations

Preparation of dense B4C ceramics by spark plasma sintering of high-purity nanoparticles

Spark plasma sintering and hot pressing of ZrB2–SiCW ultra-high temperature ceramics

Properties and Microstructure of an HfB2-HfC-SiC Ultra High Temperature Ceramics