MgB2 Films Prepared by Rapid Annealing Method

Qian Dai,Xiangdong Kong,Qingrong Feng,Qianqian Yang,Huai Zhang,Ruijuan Nie,Li Han,Yanwei Ma,Furen Wang
DOI: https://doi.org/10.1016/j.physc.2012.01.014
2012-01-01
Abstract:The experiment for preparing MgB2 thin films by electron beam (e-beam) annealing of Mg-B multilayer is reported. The annealing process lasts less than 1 s, which effectively suppresses the volatility of Mg as well as the reaction of Mg and oxygen. The influence of annealing parameters on the film quality including exposure time, accelerating voltage and beam current is investigated. It is found that e-beam with lower accelerating voltage can acquire MgB2 film with smaller annealing energy density. Also, double e-beam scan annealing process helps to obtain more uniform MgB2 thin films than the single scan. This rapid annealing method synthesizes MgB2 thin films with critical temperature T-c of 35 K and critical current density J(c) at 15 K of 7.6 x 10(6) A cm(-2). (C) 2012 Elsevier B. V. All rights reserved.
What problem does this paper attempt to address?