Growth of superconducting MgB2 thin films via postannealing techniques

W.N. Kang,Eun-Mi Choi,Hyeong-Jin Kim,Hyun-Jung Kim,Sung-Ik Lee

DOI: https://doi.org/10.1016/S0921-4534%2802%2902310-9

2002-09-10

Abstract:We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at 900 C for 30 min, we obtained the best-quality MgB2 films with a transition temperature of 39 K and a critical current density of ~ 10^7 A/cm^2. Using the scanning electron microscopy, we also investigated the film growth mechanism. The samples annealed at higher temperatures showed the larger grain sizes, well-aligned crystal structures with preferential orientations along the c-axis, and smooth surface morphologies. However, a longer annealing time prevented the alignment of grains and reduced the superconductivity, indicating a strong interfacial reaction between the substrate and the MgB2 film.

Superconductivity,Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is how the superconducting properties of MgB2 thin films change under different annealing temperature and time conditions, and the influence of these conditions on the film growth mechanism. Specifically, by changing the annealing temperature (from 700°C to 950°C) and annealing time (from 30 minutes to 120 minutes), the researchers observed the influence of these parameters on the properties of MgB2 thin films such as superconducting transition temperature (\(T_c\)), critical current density (\(J_c\)), resistivity and grain size. The main purpose of the study is to find the optimal annealing conditions for preparing high - quality MgB2 thin films to improve their performance in practical applications.

Through experiments, the author found that annealing at 900°C for 30 minutes can obtain MgB2 thin films of the best quality. These films have a relatively high superconducting transition temperature (39 K) and a high critical current density (about \(10^7\) A/cm\(^2\)). In addition, the author also used a scanning electron microscope (SEM) to study the growth mechanism of the films and found that samples annealed at higher temperatures showed larger grain sizes, good crystal structure arrangements (especially the preferential orientation along the c - axis) and smooth surface morphologies. However, an overly long annealing time will hinder the arrangement of grains and reduce the superconducting properties, which indicates that annealing at high temperatures may lead to a strong interface reaction between the substrate and the MgB2 thin film.